Chem. J. Chinese Universities ›› 2014, Vol. 35 ›› Issue (7): 1596.doi: 10.7503/cjcu20140029
• Polymer Chemistry • Previous Articles Next Articles
CHEN Youning1,2, GAO Li1, HE Maofang1, WEI Yinmao1,*()
Received:
2014-01-10
Online:
2014-07-10
Published:
2014-05-26
Contact:
WEI Yinmao
E-mail:ymwei@nwu.edu.cn
Supported by:
CLC Number:
TrendMD:
CHEN Youning, GAO Li, HE Maofang, WEI Yinmao. High-capacity Polyvinyltetrazole-grafted Chelating Resin for Adsorption of Heavy Metal Ions†[J]. Chem. J. Chinese Universities, 2014, 35(7): 1596.
ATRP time /h | N content(%) (Calculated from GD) | Elemental ananlysis(%) | Surface area/ ( m2·g-1) | BJH cumulative volume/ (cm3·g-1 ) | Average pore diameter/nm | ||
---|---|---|---|---|---|---|---|
C | H | N | |||||
1 | 1.40 | 70.38 | 4.963 | 1.14 | 47.35 | 0.24 | 32.24 |
3 | 4.07 | 69.20 | 5.381 | 3.14 | 45.14 | 0.23 | 25.06 |
5 | 6.45 | 69.20 | 5.210 | 5.04 | 40.06 | 0.21 | 23.65 |
10 | 9.19 | 65.54 | 4.305 | 8.61 | 28.81 | 0.20 | 19.71 |
Table 1 Elemental composition and physical structure parameters of PS-CH2Cl and chelating resins
ATRP time /h | N content(%) (Calculated from GD) | Elemental ananlysis(%) | Surface area/ ( m2·g-1) | BJH cumulative volume/ (cm3·g-1 ) | Average pore diameter/nm | ||
---|---|---|---|---|---|---|---|
C | H | N | |||||
1 | 1.40 | 70.38 | 4.963 | 1.14 | 47.35 | 0.24 | 32.24 |
3 | 4.07 | 69.20 | 5.381 | 3.14 | 45.14 | 0.23 | 25.06 |
5 | 6.45 | 69.20 | 5.210 | 5.04 | 40.06 | 0.21 | 23.65 |
10 | 9.19 | 65.54 | 4.305 | 8.61 | 28.81 | 0.20 | 19.71 |
Metal ion | Langmuir parameter | Freundlich parameter | ||||||
---|---|---|---|---|---|---|---|---|
Q0/(mmol·g-1) | b | Kc | KF | 1/n | ||||
Pb(Ⅱ) | 1.57 | 0.589 | 33. 72 | 0.9902 | 1.068 | 0.563 | 0.9740 | |
Ni(Ⅱ) | 1.68 | 0.645 | 36.83 | 0.9876 | 1.165 | 0.526 | 0.9642 | |
Cd(Ⅱ) | 1.92 | 0.723 | 41.17 | 0.9890 | 1.339 | 0.534 | 0.9731 |
Metal ion | Langmuir parameter | Freundlich parameter | ||||||
---|---|---|---|---|---|---|---|---|
Q0/(mmol·g-1) | b | Kc | KF | 1/n | ||||
Pb(Ⅱ) | 1.57 | 0.589 | 33. 72 | 0.9902 | 1.068 | 0.563 | 0.9740 | |
Ni(Ⅱ) | 1.68 | 0.645 | 36.83 | 0.9876 | 1.165 | 0.526 | 0.9642 | |
Cd(Ⅱ) | 1.92 | 0.723 | 41.17 | 0.9890 | 1.339 | 0.534 | 0.9731 |
Adsorbent | Metal ion | Sorption capacity/ (mmol·g-1) | Ref. |
---|---|---|---|
Poly(hydroethylacrylate)-grafted crosslinked poly(vinyl chloride) particles | Cu(Ⅱ), Zn(Ⅱ), Cd(Ⅱ) | (35—60)×10-3 | [ |
Amine and thio chelating resins | Hg(Ⅱ), Cd(Ⅱ), Zn(Ⅱ) | 1.73,0.69,0.65 | [ |
Amine-functionalised SBA-15 | Pb(Ⅱ), Cd(Ⅱ) | 39×103, 41×103 | [ |
N,N'-di(carboxymethyl) dithiocarbamate chelating resin | Pb(Ⅱ), Cu(Ⅱ), Ni(Ⅱ) | 1.40,1.08,0.97 | [ |
Magnetic beads with amino groups | Cu(Ⅱ), Ni(Ⅱ) | 0.814,0.845 | [ |
Poly(amidoxime)/SiO2 | Ni(II), Pb(Ⅱ), Cd(Ⅱ) | 0.55,0.42,0.35 | [ |
Poly(Hydroxyethyl methacrylate/Maleamic acid)[p(HEA/MALA)] hydrogel | Ni(II), Pb(Ⅱ), Cd(Ⅱ) | 0.2,0.244,0.18 | [ |
PVT-g-PS resin | Pb(Ⅱ), Ni(Ⅱ), Cd(Ⅱ) | 1.57,1.68,1.92 | This study |
Table 3 Comparison of heavy metal ions adsorption capacity of various adsorbents
Adsorbent | Metal ion | Sorption capacity/ (mmol·g-1) | Ref. |
---|---|---|---|
Poly(hydroethylacrylate)-grafted crosslinked poly(vinyl chloride) particles | Cu(Ⅱ), Zn(Ⅱ), Cd(Ⅱ) | (35—60)×10-3 | [ |
Amine and thio chelating resins | Hg(Ⅱ), Cd(Ⅱ), Zn(Ⅱ) | 1.73,0.69,0.65 | [ |
Amine-functionalised SBA-15 | Pb(Ⅱ), Cd(Ⅱ) | 39×103, 41×103 | [ |
N,N'-di(carboxymethyl) dithiocarbamate chelating resin | Pb(Ⅱ), Cu(Ⅱ), Ni(Ⅱ) | 1.40,1.08,0.97 | [ |
Magnetic beads with amino groups | Cu(Ⅱ), Ni(Ⅱ) | 0.814,0.845 | [ |
Poly(amidoxime)/SiO2 | Ni(II), Pb(Ⅱ), Cd(Ⅱ) | 0.55,0.42,0.35 | [ |
Poly(Hydroxyethyl methacrylate/Maleamic acid)[p(HEA/MALA)] hydrogel | Ni(II), Pb(Ⅱ), Cd(Ⅱ) | 0.2,0.244,0.18 | [ |
PVT-g-PS resin | Pb(Ⅱ), Ni(Ⅱ), Cd(Ⅱ) | 1.57,1.68,1.92 | This study |
[1] | Zhang Y., Qu R. J., Sun C. M., Chen H., Wang C. H., Ji C. N., Yin P., Sun Y. F., Zhang H., Niu Y., J. Hazard. Mater., 2009, 163, 127—135 |
[2] | Zhang Y. L., Fang T., Yu X. J., Chem. Res. Chinese Universities, 2013, 29(1), 144—149 |
[3] | Guibal E., Sep. Purif. Technol., 2004, 38, 43—74 |
[4] | Liu P., Liu W. M., Xue Q. J., J. Macromol. Sci.: Pure Appl. Chem., 2004, 41, 1001—1010 |
[5] | Abd EI-Wahab H., Abd EL-Fattah M., Ghazy M. B. M., Prog. Org. Coat., 2011, 72, 353—359 |
[6] | Bernard J., Branger C., Beurroies I., Denoyel R., Margaillan A., React. Funct. Polym., 2012, 72, 98—106 |
[7] | Dong J. B., Wu J. B., Yang J., Song W., Dai X. J., Ye Z. D., Gong B. L., Chem. J. Chinese Universities, 2013, 34(3), 714—719 |
(董佳斌, 吴建波, 杨静, 宋玮, 戴小军, 冶正得, 龚波林. 高等学校化学学报, 2013, 34(3), 714—719) | |
[8] | Tsyurupa M. P., Davankov V. A., React. Funct. Polym., 2006, 66, 768—779 |
[9] | Sun Y., Zhang L., Xu F., Gong B. L., Chem. J. Chinese Universities, 2012, 33(12), 2644—2650 |
(孙杨, 张雷, 徐飞, 龚波林. 高等学校化学学报, 2012, 33(12), 2644—2650 | |
[10] | Wang F. Q., Hao J. X., Dai X. J., Gong B. L., Chem. J. Chinese Universities, 2011, 32(12), 2757—2762 |
(王富强, 郝俊霞, 戴小军, 龚波林. 高等学校化学学报, 2011, 32(12), 2757—2762) | |
[11] | Zong G. X., Chen H., Qu R. J., Wang C. H., Ji N. Y., J. Hazard. Mater., 2011, 186, 614—621 |
[12] | Bhut B.V., Husson S. M., J. Membr. Sci., 2009, 337, 215—223 |
[13] | Wei Y. M., Ma J. J., Wang C. Z., J. Membr. Sci., 2013, 427, 197—206 |
[14] | Qian X. L., Fan H., Wang C. Z., Wei Y. M., Appl. Surf. Sci., 2013, 271, 240—247 |
[15] | Wang Q. H., Wang C. Z., Wei Y. M., Chem. J. Chinese Universities, 2012, 33(11), 2579—2584 |
(王琴会, 王超展, 王引茂. 高等学校化学学报, 2012, 33(11), 2579—2584) | |
[16] | Gao B. J., Gao Y. C., Li Y. B., Chem. Eng. J., 2010, 158, 542—549 |
[17] | Sun J., Chen Z. M., Ge M. Y., Xu L., Zhai M. L., J. Hazard. Mater., 2013, 244—245, 94—101 |
[18] | Lei G. H. , Xiong X. H., Huo Y. M., Wei Y. M., Zheng X. H., Chem. J. Chinese Universities, 2008, 29(2), 268—272 |
(雷根虎, 熊晓虎, 霍艳敏, 卫引茂, 郑晓晖. 高等学校化学学报, 2008, 29(2), 268—272) | |
[19] | Gaponiki P. N., Ivashkevich O. A., Karavai V. P. A. I., Chernavina N. I., Sukhanov G. T., Gareev G. A., Makromol. Chem., 1994, 219, 89 |
[20] | Zong G. X., Chen H., Qu R. J., Wang C. H., Ji N. Y., J. Hazard. Mater., 2011, 186, 614—621 |
[21] | Zachary P. D., Sharpless K. B., Org. Lett., 2002, 4(15), 2525—2527 |
[22] | Yan S. H., Zhao M., Lei G. H., Wei Y. M., J. Appl. Polym. Sci., 2012, 125, 382—389 |
[23] | Chen Y.N., He M. F., Wang C. Z., Wei Y. M.,J. Mater. Chem. A, 2014, DOI: 10.1039/C4TA01512F |
[24] | Huang M. R., Li X. G., Li S. X., Zhang W., React. Funct. Polym., 2004, 59, 53—61 |
[25] | Koldobskii G. I., Ostrovskii V. A., Chem. Heterocycl. Compd.(USSR), 1988, 5, 469—480 |
[26] | Kumar Y. P., King P., Prasad V. S. R. K., J. Hazard. Mater, 2006, 137(2), 1211—1217 |
[27] | Liu P., Liu Y. S., Su Z. X., Ind. Eng. Chem. Res., 2006, 45, 2255—2260 |
[28] | Atia A. A., Donia A. M., Yousif A. M., React. Funct. Polym., 2003, 56 ,75—82 |
[29] | Colm M. M., Aoife M. B., Justin D. H., Michael A. M., J. Colloid Interface Sci., 2012, 369, 330—337 |
[30] | Jing X. S., Liu F. Q., Yang X., Ling P. P., Li L. J., Long C., Li A. M., J. Hazard. Mater., 2009, 167, 589—596 |
[31] | Lin Z., Zhang Y., Chen Y., Qian H., Chem. Eng. J., 2012, 200-202(200), 104—110 |
[32] | Wu N. M., Li Z. K., Chem. Eng. J., 2013, 215216, 894—902 |
(Ed.: W, Z) |
[1] | LI Hua, YANG Ke, HUANG Junfeng, CHEN Fengjuan. Design and Construction of UiO-66-NH2/wood Composite for Efficient Removal of Trace Heavy Metal Ions from Water [J]. Chem. J. Chinese Universities, 2022, 43(3): 20210701. |
[2] | MA Jianxin, LIU Xiaodong, XU Na, LIU Guocheng, WANG Xiuli. A Multi-functional Zn(II) Coordination Polymer with Luminescence Sensing, Amperometric Sensing, and Dye Adsorption Performance [J]. Chem. J. Chinese Universities, 2022, 43(1): 20210585. |
[3] | ZHAO Kaiqing, WU Ruoyu, LUO Yifeng, SHI Chunhong, HU Jun. Construction of Active Sites in Porous Organic Polymers for Various Heavy Metal Ions Capture [J]. Chem. J. Chinese Universities, 2021, 42(3): 834. |
[4] | LIU Shuaizhuo,ZHANG Qian,LIU Ning,XIAO Wenyan,FAN Leiyi,ZHOU Ying. One-step Synergistic Hydrophobic Modification of Melamine Sponge and Its Application [J]. Chem. J. Chinese Universities, 2020, 41(3): 521. |
[5] | WU Shanshan,WEI Chanling,ZHAO Lijuan,TIAN Yang,WANG Xia,GONG Bolin. Preparation and Enrichment Properties of Novel Magnetic Restricted Access Media-molecularly Imprinted Composites† [J]. Chem. J. Chinese Universities, 2019, 40(6): 1150. |
[6] | JI Yuchun,MAO Wenhui,LIAO Hejie,WANG Jilin,LONG Fei,GU Yunle. Boron Nitride Nanotube-nanosheet Hierarchical Structures andIts Optical/adsorption Properties† [J]. Chem. J. Chinese Universities, 2019, 40(2): 216. |
[7] | KANG Yuanyuan, GUO Zeqing, ZHOU Jianping. Hydrothermal Preparation and Adsorption Property of MoS2/Na2Fe2Ti6O16† [J]. Chem. J. Chinese Universities, 2018, 39(7): 1364. |
[8] | GUO Ming, ZHANG Xinge, ZENG Chuchu, YIN Xinxin. Preparation and Properties Characterization of Intelligent Molecularly Imprinted Polymer Based on Diles-Alder Reaction† [J]. Chem. J. Chinese Universities, 2018, 39(3): 566. |
[9] | BULIN Chaoke, GUO Ting, ZHANG Bangwen, DAI Zhian, YU Huitao, XING Ruiguang, ZI Luxiong. Fast Removal of Aqueous Mn(Ⅱ) Using Partially Reduced Graphene Oxide-Fe3O4† [J]. Chem. J. Chinese Universities, 2017, 38(2): 217. |
[10] | WANG Huili, ZHAO Yue, MA Lekuan, FAN Penghao, XU Congbin, JIAO Chunlei, LIN Aijun. Preparation of Composite Modified Expanded Graphite and Its Adsorption on Acid Brilliant Blue Dye† [J]. Chem. J. Chinese Universities, 2016, 37(2): 335. |
[11] | XU Junge, LI Yunqin, YUAN Baoling, CUI Haojie, FU Minglai. Synthesis and Characterization of 3D Flower-like α-FeOOH Nanostructures† [J]. Chem. J. Chinese Universities, 2015, 36(1): 48. |
[12] | WANG Zitao, XIAO Changfa, ZHAO Jian, HU Xiao, XU Naiku. Preparation of Reduced Graphene Oxide-based Melamine Sponge and Its Absorption Properties† [J]. Chem. J. Chinese Universities, 2014, 35(11): 2410. |
[13] | MA Chao, XU Yan, GUO Xin-Yu, LUO Xiang-Ren, WU Xue-Min. Adsorption Properties of Comb-shaped Copolymer of Polycarboxylic Acid Superplasticizer on the Interface of Fipronil Particles [J]. Chem. J. Chinese Universities, 2013, 34(6): 1441. |
[14] | DONG Jia-Bin, WU Jian-Bo, YANG Jing, SONG Wei, DAI Xiao-Jun, YE Zheng-De, GONG Bo-Lin. Preparation of High-capacity IDA Chelating Resin and Its Adsorption Properties [J]. Chem. J. Chinese Universities, 2013, 34(3): 714. |
[15] | LU Wen-Guan, LIU Hong-Wen, YIN Xu-Guang, LAN Lu-Mei, LIU Hai-Yao. Diverse Structures of Two Zn(Ⅱ) Coordination Polymers with 5-Amino-tetrazolate and 1,4-Benzenedicarboxylate Tuned by Solvent System [J]. Chem. J. Chinese Universities, 2013, 34(12): 2691. |
Viewed | ||||||
Full text |
|
|||||
Abstract |
|
|||||