高强度聚乙烯醇水凝胶微球的制备

高素照, 陈际达, 亓倩倩, 舒荣德, 邱智萍, 任竞争   

  1. 重庆大学化学化工学院, 重庆 400030
  • 收稿日期:2010-12-01 修回日期:2011-02-23 出版日期:2011-10-10 发布日期:2011-09-11
  • 通讯作者: 陈际达 E-mail:chencqu@cqu.edu.cn
  • 基金资助:

    重庆市自然科学基金(批准号: CSTC2008BB4056)和重庆大学211工程三期创新人才培养计划建设项目(批准号: S-09103)资助.

Preparation of Polyvinyl Alcohol Hydrogel Microspheres with High Strength

GAO Su-Zhao, CHEN Ji-Da*, QI Qian-Qian, SHU Rong-De, QIU Zhi-Ping, REN Jing-Zheng   

  1. College of Chemistry and Chemical Engineering, Chongqing University, Chongqing 400044, China
  • Received:2010-12-01 Revised:2011-02-23 Online:2011-10-10 Published:2011-09-11
  • Contact: CHEN Ji-Da E-mail:chencqu@cqu.edu.cn
  • Supported by:

    重庆市自然科学基金(批准号: CSTC2008BB4056)和重庆大学211工程三期创新人才培养计划建设项目(批准号: S-09103)资助.

PDF (PC)

被引次数

16

摘要： 以三氯甲烷/丙酮为凝固液, 用高压静电技术制备了高强度、物理交联的聚乙烯醇(PVA)水凝胶微球. 研究了凝固液组成、PVA溶液浓度、温度和湿度、电场强度、进样速度及微球冷冻次数等对PVA微球的形貌、粒径和强度的影响. 结果表明, 采用常压水蒸气控制PVA溶液温度与湿度的高压静电技术, 可克服高浓度PVA溶液在强电场下出现微丝现象, 形成的水凝胶微球具有强度高、粒径在一定范围内可控的特点.

关键词: 高压静电法, 物理交联, 聚乙烯醇水凝胶微球, 组织工程

Abstract: Physical cross-linked polyvinyl alcohol(PVA) hydrogel microspheres with high strength were prepared by a modified high-voltage electrostatic technique. The hydrogel microspheres were solidified and suspended in coagulation liquid composed of chloroform and acetone, then the microspheres in coagulation liquid were frozen and thawed to get PVA cross\|linked. The influence factors of PVA microspheres' diameter and morphology, such as, coagulation liquid, PVA solution concentration and flow rate, temperature and humidity and electrostatic field strength of high-voltage electrostatic system, the number of froze and thaw cycle of PVA were investigated. The results showed that high-voltage electrostatic system modified with atmospheric steam to control temperature and humidity  of PVA microsphere formation area was an effective method to overcome microfilament formation while PVA solution was in higher concentration, the optimized condition for prepare PVA hydrogel microspheres with high strength and controlled diameter was coagulation liquid of chloroform/acetone(2∶1, volume ratio), frozen at -20 ℃ and thawed at room temperature for five cycles, PVA solution concentration of 12% in weight, flow rate of 2 mL/h, electrostatic field strength of 12-15 kV, electrode distance of 3 cm, and the PVA hydrogel microsphere has a widely potential use in the field of tissue engineering.

Key words: High-voltage electrostatic, Physical cross-linking, Polyvingl alchol(PVA) hydrogel microsphere, Tissue engineering