高等学校化学学报 ›› 2005, Vol. 26 ›› Issue (8): 1387.

• 研究论文 • 下一篇

氢氧化镍纳米棒的水热制备及其表征

田周玲, 矫庆泽, 赵芸

北京理工大学化工与环境学院, 北京100081

收稿日期:2004-12-07 出版日期:2005-08-10 发布日期:2005-08-10
通讯作者: 矫庆泽(1960年出生),男,博士,教授,主要从事功能材料研究.E-mail:jiaoqz@bit.edu.cn E-mail:jiaoqz@bit.edu.cn
基金资助:
国防“十五”预研基金(批准号:41328030507)资助.

Preparation and Characterization of Nickel Hydroxide Nanorods Using Hydrothermal Synthesis Method

TIAN Zhou-Ling, JIAO Qing-Ze, ZHAO Yun

School of Chemical Engineering & Environment, Beijing Institute of Technology, Beijing 100081, China

Received:2004-12-07 Online:2005-08-10 Published:2005-08-10

摘要/Abstract

摘要： 以Ni₂SO₄·6H₂O和NaOH为原料,在水热条件下制备了氢氧化镍纳米棒.运用透射电子显微镜(TEM)和X射线衍射仪(XRD)对样品进行了表征,考察了水热反应温度和pH值对产物的形貌和结构的影响.结果表明,氢氧化镍纳米棒形成的最佳条件是180～200℃,pH为9～10.

关键词: 氢氧化镍, 纳米棒, 水热合成

Abstract: Nickel hydroxide nanorods were prepared by using hydrothermal synthesis method. The structures of Ni(OH)₂ were characterized by X-ray diffractometer. The morphologies were observed by using TEM. The influences of hydrothermal reaction temperature and pH values on the morphologies and structure of the products were investigated. It was found that the best conditions for preparing nickel hydroxide nanorods were the reaction temperature in the range 180～200 ℃ and the pH value between 9 and 10.

Key words: Nickel hydroxide, Nanorods, Hydrothermal synthesis

中图分类号:

O614.4

TrendMD:

田周玲, 矫庆泽, 赵芸. 氢氧化镍纳米棒的水热制备及其表征. 高等学校化学学报, 2005, 26(8): 1387.

TIAN Zhou-Ling, JIAO Qing-Ze, ZHAO Yun . Preparation and Characterization of Nickel Hydroxide Nanorods Using Hydrothermal Synthesis Method. Chem. J. Chinese Universities, 2005, 26(8): 1387.

参考文献

[1] Zhou S.X.,Li J.M.,Ke Y.X.et al..Mater.Lett.[J],2003,57:2602_2605 [2] Cao M.H.,Hu C.W.,Wang Y.H.et al..Chem.Comm un.[J],2003:1884_1885 [3] GU O Min(郭敏),D IAO Peng(刁鹏),CA I Sheng-Min(蔡生民).Chem.J.Ch inese Un iversities(高等学校化学学报)[J],2004,25(2):345_347 [4] Hu J.Q.,Deng B.,Zhang W.X.et al..In ter.J.Ino rg.Mater.[J],2001,3:639_642 [5] Nie Q.L.,Xu Z.D.,Yuan Q.L.et al..Mater.Chem.Phys.[J],2003,82:808—811 [6] GU O Bing-Kun(郭炳),L I Xin-Hai(李新海),YAN G Song-Qing(杨松青).Chem istry Electrical Sou rce——Battery Princip le and Prep aration Techno logy(化学电源——电池原理及制备技术)[M],Chang sha:Cen tral Sou th Un iversity Press,2003:208_209 [7] Cai F.S.,Zhang G.Y.,Chen J.et al..Angw.Chem.In t.Ed s.[J],2003,43(32):4212_4216 [8] ZHAO Li(赵力),ZHOU De-Ru i(周德瑞),ZHAN G Cu i-Fen(张翠芬).Chem.On line(化学通报)[J],2001,(8):513_515 [9] HAN Xi-Jiang(韩喜江),X IE Xiao-Mei(谢小美),XU Chong-Quan(徐崇泉)et al..Ch in.J.Ino rg.Chem.(无机化学学报)[J],2003,19(3):247_251 [10] Zhang Y.S.,Zhou Z.,Yan J..J.Pow er Sou r.[J],1998,75:283_287 [11] Liang Z.H.,Zhu Y.J.,Hu X.L..J.Phys.Chem.B[J],2004,108:3488_3491 [12] Li X.L.,Liu J.F.,Li Y.D..Mater.Chem.Phys.[J],2003,80:223_227 [13] Liang J.H.,Li Y.D..Chem.Lett.[J],2003,32(12):1126_1127 [14] L I Shu-Tang(李树棠).Elem en ts of X-ray Diffraction fo r Crystal(晶体X射线衍射学基础)[M],Chang sha:Met allu rgy Press, 1990:106_109 [15] XU Ru-Ren(徐如人),PAN G Wen-Qin(庞文琴).Ino rgan ic Syn thesis and Prep arative Chem istry(无机合成与制备化学)[M], Beijing:Higher Education Press,1991:133_134 [16] Wang X.,Li Y.D..Angew.Chem.In t.Ed.[J],2002,41(24):4790_4793 [17] Wang X.,Li Y.D..Chem.Eu r.J.[J],2003,9(1):300_306 [18] Peng Z.A.,Peng X.G..J.Am.Chem.Soc.[J],2001,123:1389_1395 [19] Peng Z.A.,Peng X.G..J.Am.Chem.Soc.[J],2002,124:3343_3353

氢氧化镍纳米棒的水热制备及其表征

Preparation and Characterization of Nickel Hydroxide Nanorods Using Hydrothermal Synthesis Method

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	梁宇, 刘欢, 宫丽阁, 王春晓, 王春梅, 于凯, 周百斌. 联咪唑修饰{SiW₁₂O₄₀}杂化物的合成及超级电容性能[J]. 高等学校化学学报, 2022, 43(1): 20210556.
[2]	陆峰, 贡祎, 赵婷, 赵宁, 琚雯雯, 范曲立, 黄维. 二元混合表面活性剂用于窄吸收金纳米棒的无种子合成[J]. 高等学校化学学报, 2021, 42(3): 700.
[3]	张会双, 高延晓, 王秋娴, 李向南, 刘文凤, 杨书廷. CTAB辅助水热合成高镍三元材料LiNi_0.6Co_0.2Mn_0.2O₂及其高低温性能研究[J]. 高等学校化学学报, 2021, 42(3): 819.
[4]	王冶, 张晓思, 孙丽婧, 李冰, 刘琳, 杨淼, 田鹏, 刘仲毅, 刘中民. 有机硅烷辅助合成特殊形貌SAPO分子筛[J]. 高等学校化学学报, 2021, 42(3): 683.
[5]	王健羽, 张强, 闫文付, 于吉红. 羟基自由基在沸石分子筛合成中的作用[J]. 高等学校化学学报, 2021, 42(1): 11.
[6]	吴勤明, 王叶青, 孟祥举, 肖丰收. 硅铝沸石分子筛晶化过程再思考[J]. 高等学校化学学报, 2021, 42(1): 21.
[7]	刘亚冰,李明阳,田戈,阿拉腾沙嘎,裴桐鹤,聂婧思. 基于2-氨基吡啶的两个簇基超分子化合物的合成、结构及催化性能[J]. 高等学校化学学报, 2020, 41(5): 995.
[8]	卓孟宁,李飞,蒋浩,陈倩文,李鹏,王立章. SnO₂/GDE阴极的制备及电催化还原CO₂产甲酸性能[J]. 高等学校化学学报, 2020, 41(3): 530.
[9]	欧阳密, 陈璐, 胡旭明, 李裕文, 戴大程, 屠袁波, 白茹, 吕晓静, 张诚. TiO₂-PTPAT纳米核/壳结构复合膜的制备及电致变色性能[J]. 高等学校化学学报, 2020, 41(12): 2796.
[10]	董乐, 黄星亮, 任俊杰, 代小平, 刘宗俨, 田洪锋, 王志东, 吴晓彤. 硅溶胶粒度与分布对高硅铝比镁碱沸石合成的影响机理[J]. 高等学校化学学报, 2020, 41(11): 2449.
[11]	周海, 陈豪, 郭娅, 康敏. 介孔Co₃O₄多面体的制备及电化学性能[J]. 高等学校化学学报, 2019, 40(7): 1374.
[12]	高宁萧, 徐玉龙, 刘勇. 豆奶粉提取碳点及含碳点荧光纳米纤维的制备[J]. 高等学校化学学报, 2019, 40(3): 555.
[13]	宋子琦, 公柏娟, 王璐, 冯婧, 王博, 闫弘静, 李志民, 孙宏晨. 聚多巴胺包覆的金纳米棒用于大鼠下颌下腺造影成像[J]. 高等学校化学学报, 2019, 40(1): 166.
[14]	潘帅, 胡校兵, 宋润民, 解丽丽, 朱志刚, 郑嘹赢. 醋酸钾溶液体系中α-Fe₂O₃纳米微球的离子液体辅助合成及气敏性能研究[J]. 高等学校化学学报, 2018, 39(8): 1631.
[15]	夏坤, 周丹, 杨赟, 杨水金, 夏清华. 高度均一的AlPO₄-11微晶的高效合成及晶化过程研究[J]. 高等学校化学学报, 2018, 39(8): 1624.