膨胀石墨层间生长高活性氧化锌及其光催化性能

蒋保江1,2, 王鹏飞2, 侯宗伟2, 乔英杰1, 付宏刚2   

  1. 1. 哈尔滨工程大学材料科学与化学工程学院, 哈尔滨 150001;
    2. 黑龙江大学功能无机材料化学教育部重点实验室, 哈尔滨 150080
  • 收稿日期:2012-01-12 出版日期:2012-11-10 发布日期:2012-10-15
  • 通讯作者: 乔英杰,男,博士,教授,博士生导师,主要从事结构功能一体化材料研究.E-mail:qiaoyingjie@hrbeu.edu.cn;付宏刚,男,博士,教授,博士生导师,主要从事晶态材料设计及性能研究.E-mail:fuhg@vip.sina.com E-mail:qiaoyingjie@hrbeu.edu.cn;fuhg@vip.sina.com
  • 基金资助:

    国家自然科学基金重点项目(批准号: 21031001)资助.

In situ Growth of Zinc Oxide within Expended Graphite and Enhanced Photocatalytic Performance

JIANG Bao-Jiang1,2, WANG Peng-Fei2, HOU Zong-Wei2, QIAO Ying-Jie1, FU Hong-Gang2   

  1. 1. College of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China;
    2. Key Laboratory of Functional Inorganic Material Chemistry, Ministry of Education, Heilongjiang University, Harbin 150080, China
  • Received:2012-01-12 Online:2012-11-10 Published:2012-10-15
  • Contact: Hong-Gang FU E-mail:qiaoyingjie@hrbeu.edu.cn;fuhg@vip.sina.com

摘要:

以醋酸锌和膨胀石墨为原料, 采用真空辅助压力诱导手段使反应溶液注入膨胀石墨层间, 在180℃下溶剂热反应12 h, 一步得到氧化锌纳米棒/石墨烯复合光催化剂, 采用X射线衍射仪(XRD)和透射电子显微镜(TEM)等对复合光催化剂的结构和形貌进行了表征. 结果表明, 合成的氧化锌纳米棒具有六方晶系纤锌矿结构; 氧化锌纳米棒在石墨烯表面分散性较好, 其平均直径约50 nm, 长度约150~200 nm. 所得氧化锌纳米棒/石墨烯复合材料对亚甲基蓝的降解效率优于目前应用最广泛的光催化剂Degussa P25.

关键词: 氧化锌纳米棒/石墨烯复合体, 亚甲基蓝, 光催化, 膨胀石墨

Abstract:

Zinc acetate and expanded graphite were selected as raw material. Under vacuum, the initial reaction solution was infused in the interlayers of expanded graphite. Then, zinc oxide nanorods/graphene compo-sites were prepared by solvothermal method at 180℃ for 12 h. The structure and the morphology of \{products were characterized by X-ray diffraction(XRD) and transmission electron microscopy(TEM). The results show that the zinc oxide nanorods uniformly grow on the surface of graphene sheets. The average diameter of rod-like zinc oxide is about 50 nm, and the length is about 150-200 nm. The zinc oxide nanorods/graphene compo-sites exhibited high photocatalytic activity in the degradation of methylene blue under UV lights in comparison with bare Degussa P25.

Key words: Zinc oxide nanorods/graphene composites, Methylene blue, Photocatalysis, Expanded graphite