Preparation of Highly Dispersed Supported Metal Catalysts via Sol vated Metal Atom Impregnation (Ⅶ)--The Structures and Properties of Ni-Cu/SiO2Bimetallic Catalysts

Abstract

Abstract: Ni-Cu/SiO₂catalysts with different compositions were prepared by metal vapor method. XRD, TEM and magnetic measurements showed that Ni-Cu alloy was formed, the composition of the alloy particles were nonuniform and some free Ni and Cu atoms also existed, the metallic particle size depended on the atomic ratios Ni/Cu. As the Cu content increased, the metallic particle size increased and varied between 30-100Å. XPS observations revealed that Ni was in zero, +1, and +2 valence states. Cu mainly existed as metallic Cu and Partly as Cu₂O. The results of XPS also show that the surface compositions of these catalysts were different from those of their bulk. In contrast with the surface enrichment in copper generally observed on Ni -Cu catalysts, the surfaces of these catalyst were enriched in nickel. The results of hydrogenation of furfural showed that the activity of bimetallic catalyst with Ni/Cu molar ratio 1 : 1 was greater than those with Ni/Cu2:1 and 3:1, and those of Ni(or Cu) monometallic catalysts.

Key words: Metal vapor synthesis, Ni-Cu bimetallic catalysts, Magnetic property, XPS (Y,X)

TrendMD:

Wu Shi-hua, Huang Wei-ping, Wang Xu-kun, Liu Shang-yuan . Preparation of Highly Dispersed Supported Metal Catalysts via Sol vated Metal Atom Impregnation (Ⅶ)--The Structures and Properties of Ni-Cu/SiO₂Bimetallic Catalysts[J]. Chem. J. Chinese Universities, 1991, 12(8): 1099.

References

Related Articles 15

[1]	Baozhen SHI,Shan LI,Dianpeng WANG,Yunzhi ZHOU,Jinyu SUN. Synthesis and Physical Properties of Cobalt-Zinc Hybrid Porous Metal-organic Frameworks ^† [J]. Chem. J. Chinese Universities, 2019, 40(12): 2443.
[2]	JIANG Xianming,WANG Huaiqian,CAO Yu,SUN Zhihui,CAO Yufang,WU Weibin. Structure Prediction and Photoelectron Spectroscopy Study of Rare Earth-doped Silicon-based Clusters of MS $i q 7$ (M=Eu, Sm, Yb; q=0, -1)^† [J]. Chem. J. Chinese Universities, 2018, 39(9): 1976.
[3]	LIU Jingwei,YU Guangtao,SHEN Xiaopeng,HUANG Xuri,CHEN Wei. Theoretical Studies on the Structures, Electronic and Magnetic Properties of Fully and Partically Fluorizated Germanene Nanoribbons^† [J]. Chem. J. Chinese Universities, 2018, 39(5): 977.
[4]	CONG Rimin, YU Huaiqing, LUO Yunjun, LI Jiao, WANG Weiwei, LI Qiuhong, SUN Wuzhu, SI Weimeng, ZHANG Hua. Synthesis and Properties of Bi₂₅FeO₄₀/α-Fe₂O₃ Composite Nanoparticle Photocatalysts^† [J]. Chem. J. Chinese Universities, 2018, 39(4): 629.
[5]	XU Shenghua, XIA Pengfei, ZHANG Kunxi, GAO Long, YIN Jingbo. Fabrication and Performance for Fe₃O₄ Nanoparticles Surface Grafted Poly(γ-benzyl-L-glutamate) Porous Microcarriers^† [J]. Chem. J. Chinese Universities, 2017, 38(7): 1295.
[6]	YANG Yuxiang, LIU Yicheng, ZHAO Min, YUAN Hongming, YAO Pingping, HUANG Yan, NI Chaoying. Thermal Reduation Preparation of Co²⁺/Dy³⁺ Doped Cubic Fe₃O₄ and Their Magnetic Targeting Retention^† [J]. Chem. J. Chinese Universities, 2017, 38(10): 1709.
[7]	MA Benhua, PENG Yu, HUA Jia, SHI Zhan. Synthesis and Characterization of Coordination Polymers Based on 5-Azidoisophthalic Acid^† [J]. Chem. J. Chinese Universities, 2015, 36(2): 215.
[8]	LIU Yabing, DUAN Weijie, CUI Xiaobing, XU Jiqing. Synthesis and Characterization of a 2D Tungstovanadated Derivative: [Cu(en)₂]₂[V^ⅤO₄₄{Cu(en)₂(H₂O)}₂]·3H₂O^† [J]. Chem. J. Chinese Universities, 2015, 36(1): 34.
[9]	HE Yongke, YAN Yan, YANG Fen, WU Junbiao, SONG Xiaowei. Ionothermal Syntheses and Characterization of Open-framework Manganese Phosphites (NH₄)₂Mn₃(HPO₃)₄ and Mn(HPO₃)^† [J]. Chem. J. Chinese Universities, 2014, 35(9): 1859.
[10]	XU Man, DUAN Weijie, JIAO Shihui, PANG Guangsheng. Preparation and Magnetic Performance of Fe₃O₄/TiO₂Hybrid Nanostructure^† [J]. Chem. J. Chinese Universities, 2014, 35(5): 917.
[11]	WANG Yanyan, ZHANG Zheng, SUN Yanjun, LI Jiyang. Synthesis and Characterization of a New Open-framework Iron Phosphate^† [J]. Chem. J. Chinese Universities, 2014, 35(3): 449.
[12]	LIU Yan-Qing, WU Yu-Han, LI Dan, ZHANG Jing, ZHANG Yong-Jun, YANG Jing-Hai. Synthesis and Properties of NiFe₂O₄/BaTiO₃ Multiferroic Composites [J]. Chem. J. Chinese Universities, 2013, 34(2): 313.
[13]	XU Feng, XIANG Chen, LI Liang-Chao, MAO Meng-Yi, ZHOU Yan, DING Yan, LI Juan-Bi. Preparation and Electromagnetic Properties of CoFe₂O₄ and Its Composites with Expanded Graphite [J]. Chem. J. Chinese Universities, 2013, 34(10): 2254.
[14]	WANG Lei, WANG Yan-Yan, LI Yi, LIANG Zhi-Qiang. Synthesis and Characterization of a Novel Mixed-valence Vanadogermanate Cluster [Ge₆V₆^VV₉^ⅣO₄₂(OH)₆(H₂O)] [J]. Chem. J. Chinese Universities, 2012, 33(08): 1646.
[15]	WANG Yi-Long, ZHANG Huan, ZHAO Su-Ling. Controlled Fabrication of Mn_0.6Zn_0.4Fe₂O₄ Magnetic Submicrospheres and Their Magnetic Properties [J]. Chem. J. Chinese Universities, 2012, 33(07): 1376.

Preparation of Highly Dispersed Supported Metal Catalysts via Sol vated Metal Atom Impregnation (Ⅶ)--The Structures and Properties of Ni-Cu/SiO₂Bimetallic Catalysts

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments