Preparation of the Blend Membranes Based on Sulfonated Polyetheretherketoneketone and Amine-terminated Hyperbranched Polyimide

WANG Peng1, WU Xian2, ZHANG Hanyu1, YOU Kaiyuan1, LIU Zhenchao1, LIU Baijun1,*()   

  1. 1. National & Local Joint Engineering Laboratory for Synthesis Technology of High-performance Polymers, Key Laboratory of High-performance Plastics, Ministry of Education, College of Chemistry, Jilin University, Changchun 130012, China
    2. College of Materials Science and Engineering, Jilin University, Changchun 130012, China
  • Received:2017-12-01 Online:2018-03-10 Published:2018-01-23
  • Contact: LIU Baijun E-mail:liubj@jlu.edu.cn

摘要:

关键词: 超支化聚合物, 聚芳醚酮, 磺化, 质子交换膜, 聚酰亚胺

Abstract:

An amine-terminated hyperbranched polyimide(Am-HBPI) was introduced into a sulfonated flurenyl-containing polyetheretherketoneketone(SFPEEKK) matrix to form “acid-base” blends for proton conductive membranes. The uniform and flexible blend membranes were obtained by a solution casting procedure with a unique phase-separation microstructure. Both TEM and SEM images clearly showed that the nano-sized Am-HBPI particles were well dispersed in SFPEEKK continuous phase. In comparison with the pristine SFPEEKK membrane, the blend membranes containing Am-HBPI “performance-enhancing component” exhibited improved dimensional stability and better mechanical properties. Meanwhile, their proton conductivity could be 0.12—0.16 S/cm at 100 ℃.

Key words: Hyperbranched polymer, Polyaryletherketone, Sulfonation, Proton exchange membrane, Polyimide(Ed.: D, Z)