Chem. J. Chinese Universities ›› 2016, Vol. 37 ›› Issue (10): 1907.doi: 10.7503/cjcu20160400

• Polymer Chemistry • Previous Articles     Next Articles

Synthesis and Characterization of Polyprrole Microcapcule Containing ZnCl2 Solution

YAO Jian, WANG Jianping*(), WEI Yao, WANG Xuechen, LI Wei, ZHANG Xingxiang   

  1. Tianjin Key Laboratory of Advanced Fibers and Energy Storage, Institute of Functional Fibers, Tianjin Polytechnic University, Tianjin 300387, China
  • Received:2016-06-02 Online:2016-10-10 Published:2016-09-20
  • Contact: WANG Jianping E-mail:jpwangcn@gmail.com
  • Supported by:
    † Supported by the National Natural Science Foundation of China(Nos;50573058, 51203113, 51573135), the Aeronautical Science Foundation of China(No.201229Q2002) and the Planned Science and Technology Project of Tianjin, China(No.09ZCKFGX02200)

Abstract:

Conductive polymer microcapsules have become a new research highlight because of its properties of both conductivity and micro/nano structure. Polypyrrole microcapsules containing ZnCl2 solution were chemically synthesized by in-situ polymerization method with water-in-oil emulsion as soft template, sodium dodecylbenzenesulfonate(DBSNa) and p-toluene sulphonic acid(TsOH) as dopants, benzoyl peroxide(BPO) as oxidant. Characterization results show that the polypyrrole microcapcules are regular core-shell structure when the concentration of ZnCl2 is 20%(mass fraction), the mass fractions of DBSNa, TsOH, BPO to the monomer are 1.27%, 4.12%, 123.71%, respectively. And the microcapcules have a fullness and smooth surface and the particle size of about 50 μm. This study is expected to expand the application of water-soluble drugs and all-solid-state ion selective electrode.

Key words: Conductive polymer, Polypyrrole, Microcapsule, Water-in-oil emulsion