新型金属有机气凝胶的合成、 表征及气体吸附性能

李湛1(), 单晓雯2(), 杨平平1, 高壮壮1, 方千荣1, 薛铭1(), 裘式纶1   

  1. 1. 吉林大学无机合成与制备化学国家重点实验室, 长春130012
    2. 中国石油化工股份有限公司青岛安全工程研究院, 青岛 266071
  • 收稿日期:2019-02-16 出版日期:2019-06-10 发布日期:2019-04-04
  • 作者简介:

    联系人简介: 薛铭, 男, 博士, 教授, 博士生导师, 主要从事无机固体材料化学的研究. E-mail: xueming@jlu.edu.cn ;单晓雯, 女, 高级工程师, 主要从事油气回收技术的研究. E-mail: shanxw.qday@sinopec.com

  • 基金资助:
    国家自然科学基金(批准号: 21571076)资助.

Preparation, Characterization and Gas Adsorption Properties of Metal-Organic Aerogels

LI Zhan1, SHAN Xiaowen2(), YANG Pingping1, GAO Zhuangzhuang1, FANG Qianrong1, XUE Ming1(), QIU Shilun1   

  1. 1. State Key Laboratory of Inorganic Synthesis & Preparative Chemistry, Jilin University, Changchun 130012, China;
    2. State Key Laboratory of Safety and Control for Chemicals, SINOPEC Research Institute of Safety Engineering, Qingdao 266101, China
  • Received:2019-02-16 Online:2019-06-10 Published:2019-04-04
  • Supported by:
    † Supported by the National Natural Science Foundation of China(No.21571076).

摘要:

利用高稳定性的UiO-66系列金属有机骨架多孔材料制备金属有机气凝胶材料, 制得的UiO-66系列金属有机气凝胶材料具有多级孔结构和较高的比表面积, 在气体吸附分离领域具有较大应用潜力. 气体吸附实验结果表明, UiO-66-NH2金属有机气凝胶材料具有极佳的CO2吸附性能和CO2/CH4分离性能, 通过理想吸附溶液理论计算得出其吸附选择性高达18.3.

关键词: 金属有机骨架多孔材料, 金属有机气凝胶, 气体吸附

Abstract:

A series of UiO-66 metal-organic frameworks(MOFs) with excellent stability was used to prepare metal-organic aerogels as a feasible way for the modeling of MOFs. The as-prepared UiO-66-based metal-organic aerogels(MOAs) possessed hierarchical pore structure and high surface area, which were very promising in gas adsorption and separation applications. In gas adsorption measurements, the amine modified UiO-66-NH2 aerogel exhibited outstanding adsorption capacity towards CO2 and high selectivity up to 18.3 towards CO2/CH4 mixture(molar ratio, 1∶1) calculated through ideal adsorbed solution theory.

Key words: Metal-organic frameworks, Aerogels, Metal-organic aerogels, Adsorption selectivity