含氨基磺化聚芳醚酮砜质子交换膜的制备与性能

徐晶美1, 程海龙1, 马丽1, 白洪伟1, 任春丽1, 张会轩1,2, 王哲1,2   

  1. 1. 长春工业大学合成树脂与特种纤维工程研究中心, 长春 130012;
    2. 中国科学院长春应用化学研究所, 长春 130012
  • 收稿日期:2013-01-21 出版日期:2013-07-10 发布日期:2013-06-21
  • 通讯作者: 王 哲, 男, 博士, 教授, 主要从事高聚物膜材料研究. E-mail: wzccut@126.com E-mail:wzccut@126.com
  • 基金资助:

    国家自然科学基金(批准号: 51273024)和吉林省教育厅项目(批准号: 2012103)资助.

Preparation and Behavior of Sulfonated Poly(aryle ether ketone sulfone) Containing Amino Proton Exchange Membrane

XU Jing-Mei1, CHENG Hai-Long1, MA Li1, BAI Hong-Wei1, REN Chun-Li1, ZHANG Hui-Xuan1,2, WANG Zhe1,2   

  1. 1. School of Chemical Engineering, Engineering Research Center of Synthetic Resin and Special Chemical Fiber, Changchun University of Technology, Changchun 130012, China;
    2. Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
  • Received:2013-01-21 Online:2013-07-10 Published:2013-06-21

PDF (PC)

被引次数

4

摘要：

通过四元缩聚的方法合成了带有氨基的磺化度可控的磺化聚芳醚酮砜共聚物(Am-SPAEKS). 采用红外光谱和核磁共振谱表征了Am-SPAEKS共聚物的结构. 该共聚物膜具有较好的热性能、尺寸稳定性、较高的质子传导率和阻醇能力. 在80℃时Am-SPAEKS-1膜的质子传导率达到0.0894 S/cm, 而其甲醇渗透系数在25℃时为0.24×10-6 cm2/s, 低于相同温度下SPAEKS膜(0.87×10-6 cm2/s)和Nafion膜(2×10-6 cm2/s). 结果表明, Am-SPAEKS膜能够满足质子交换膜燃料电池(PEMFC)的使用要求.

关键词: 氨基, 磺化聚芳醚酮砜, 质子电导率, 质子交换膜

Abstract:

The sulfonated poly(aryle ether ketone sulfone) with different sulfonation degree containing amino copolymers were prepared by polycondensation method. The FTIR and 1H NMR spectra of amino membrane-sulfonated poly(aryle ether ketone sulfone)(Am-SPAEKS) show that the amino groups are introduced into SPAEKS copolymers. The measured results show that the thermal stability, dimensional stability, resistance methanol performance and proton conductivities of Am-SPAEKS membranes are improved due to the introduction of amino groups. The proton conductivity of Am-SPAEKS-1 membrane reaches 0.0894 S/cm at 80℃. The methanol permeability coefficient of Am-SPAEKS-1 membrane is only 0.24×10-6 cm2/s, which is lower than that of pure SPAEKS(0.87×10-6 cm2/s) membrane and Nafion(2×10-6 cm2/s) membrane. All the results indicate that the Am-SPAEKS membranes are promising as proton exchange membranes for middle-high temperature proton exchange membrane fuel cells applications and direct methanol fuel cells(DMFCs).

Key words: Amino, Sulfonated poly(aryle ether ketone sulfone), Proton conductivity, Proton exchange membrane