两亲性PS-b-PEG嵌段共聚物刷的合成及响应行为

杨木泉, 毛骏, 董志鑫, 王大鹏, 姬相玲   

  1. 中国科学院长春应用化学研究所, 长春 130022
  • 收稿日期:2012-02-13 出版日期:2012-12-10 发布日期:2012-11-20
  • 通讯作者: 姬相玲,女,博士,研究员,博士生导师,主要从事高分子溶液和链结构研究.E-mail:xlji@ciac.jl.cn E-mail:xlji@ciac.jl.cn
  • 基金资助:

    国家自然科学基金(批准号: 50633030, 50621302, 5921062)资助.

Synthesis and Responsive Behavior of Amphiphilic PS-b-PEG Diblock Copolymer Brushes

YANG Mu-Quan, MAO Jun, DONG Zhi-Xin, WANG Da-Peng, JI Xiang-Ling   

  1. State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China
  • Received:2012-02-13 Online:2012-12-10 Published:2012-11-20
  • Contact: 相玲 姬 E-mail:xlji@ciac.jl.cn

PDF (PC)

被引次数

9

摘要：

利用原子转移自由基聚合(ATRP)和点击化学(Click)反应, 在硅基底上制备了聚苯乙烯-b-聚乙二醇(PS-b-PEG)两亲性嵌段共聚物刷. 首先, 利用ATRP方法在表面改性的硅片引发苯乙烯单体(St)的聚合, 得到PS-Br均聚刷, 然后通过叠氮化钠(NaN3)将均聚刷末端功能化为PS-N3, 再与炔基聚乙二醇甲醚(Alkynyl-PEG)发生Click反应, 得到PS-b-PEG嵌段共聚物刷. 通过X射线光电子能谱(XPS)和接触角测量仪表征了聚合物刷的表面化学组成和表面亲疏水性质, 证明在硅基底上接枝了嵌段共聚物刷. 用原子力显微镜(AFM)观察了PS-b-PEG嵌段共聚物刷在不同溶剂处理后的形态结构变化, 研究了其响应行为.

关键词: 聚苯乙烯-b-聚乙二醇嵌段共聚刷, 原子转移自由基聚合, 点击化学反应, 响应行为

Abstract:

Polystyrene-b-polyethylene glycol(PS-b-PEG) diblock copolymer brushes on a silicon wafer were synthesized via the combination of atom transfer radical polymerization(ATRP) and Click chemistry reaction. The ATRP initiator was grafted to silicon wafer. Then, polystyrene was grafted to the substrates through ATRP technique. After azidation with NaN3, the Si/SiO2/PS-Br brushes were transformed to Si/SiO2/PS-N3 with azide groups at the ends. The synthesis of PS-b-PEG brushes was then achieved via the click reaction of the obtained Si/SiO2/PS-N3 and an excess of alkynyl-PEG. The chemical compositions and the surface properties of the as-prepared PS-b-PEG brushes were detected via X-ray photoelectron spectroscopy(XPS), atomic force microscopy(AFM), ellipsometry, and water contact angle techniques. The responsive behavior of diblock copolymer brushes treated under different solvents was also discussed.

Key words: Polystyrene-b-polyethylene glycol diblock copolymer brush, Atom transfer radical polymerization, Click chemistry, Responsive behavior