Double Flocculation in Aqueous Dispersion of Layered Double Hydroxide Particles Induced by Sodium Polyacylate

Abstract

Abstract: The effect of sodium polyacrylate(PAAS) on the stability of aqueous dispersion of Mg/Al layered double hydroxide(MgAl-LDH) nanoparticles was studied. The adsorption of PAAS on LDH particles was determined by total organic carbon(TOC) analysis and the electrical properties of LDH particles were characterized by ζ potential measurement. The experimental results show that the LDH-PAAS mixtures appeared to be flocculation-dispersion-reflocculation as the PAAS concentration increased from 0.006 to 2.400 mmol/L in a 1.0%(mass fraction) LDH aqueous dispersion. At first, the ζ potential of LDH particles changed from positive to zero and then to negative with the increase of PAAS concentration, which was due to the adsorption of PAAS on LDH surfaces. As a result, the electrostatic repulsion between LDH particles firstly decreased and then increased. Therefore, the PAAS LDH mixture first flocculated and then dispersed. When the PAAS concentration further increased, the LDH particles remained negatively charged, and the depletion attraction between LDH particles should be the major reason causing the reflocculation of the particles. The examination of FTIR spectra of LDH, PAAS, and LDH after PAAS adsorption suggests that the adsorption of PAAS on LDH particles was mainly through the interaction between the —COO- in PAAS molecules and the LDH particles.

Key words: MgAl-Layered double hydroxide(LDH), Sodium polyacrylate(PAAS), Flocculation, Stability

TrendMD:

LIU Guo-Peng, LIU Shang-Ying, WANG Jun, SUN De-Jun*. Double Flocculation in Aqueous Dispersion of Layered Double Hydroxide Particles Induced by Sodium Polyacylate[J]. Chem. J. Chinese Universities, 2010, 31(10): 2030.

References

[1]Rives V.. Layered Double Hydroxides: Present and Future[M], Nova: Science Publishers, 2001: 1—39 [2]LEI Li-Xu(雷立旭), ZHANG Wei-Feng(张卫锋), HU Meng(胡猛), O′Hare D.. Chinese. J. Inorg. Chem.(无机化学学报)[J], 2005, 21(4): 451—463 [3]SUN De-Jun(孙德军), LIU Shang-Ying(刘尚营), YANG Zhi(杨智), ZHANG Chun-Guang(张春光). Chem. J. Chinese Universities(高等学校化学学报)[J], 2001, 22(6): 1002—1005 [4]Zhang F. Z., Xiang X., Li F., Duan X.. Catal. Surv. Asia[J], 2008, 12: 253—265 [5]Lei L. X., Khanb A., O′Hare D.. J. Solid State Chem.[J], 2005, 178: 3648—3654 [6]Wang H. Y., Schneider W. F.. J. Chem. Phys.[J], 2007, 127: 064706-1—064706-9 [7]Lei L. X., Zhang W. F., Hu M.. J. Solid State Chem.[J], 2006, 179: 3562—3567 [8]Xu Z. P., Stevenson G. S., Lu C. Q., Bartlett P. F., Gray P. P.. J. Am. Chem. Soc.[J], 2006, 128: 36—37 [9]Xu Z. P., Stevenson G. S., Lu C. Q., Lu G. Q.. J. Phys. Chem. B[J], 2006, 110: 16923—16929 [10]Wang X. J., Sun D. J., Liu S. Y., Wang R.. J. Colloid Interface Sci.[J], 2005, 289: 410—418 [11]Yang F., Liu S. Y., Xu J., Lan Q., Wei F., Sun D. J.. J. Colloid Interface Sci.[J], 2006, 302: 159—169 [12]Yang F., Niu Q., Lan Q., Sun D. J.. J. Colloid Interface Sci.[J], 2007, 306: 285—295 [13]Wang J., Yan F., Liu S. Y., Sun D. J.. Langmuir[J], 2008, 24(18): 10054—10061 [14]Liu Q., Luan L. Y., Sun D. J., Xu J.. J. Colloid Interface Sci.[J], 2010, 343: 87—93 [15]Kang H. L., Huang G. L., Ma S. L., Bai Y. X., Ma H., Li Y. L., Yang X. J.. J. Phys. Chem. C[J], 2009, 113: 9157—9163 [16]Gregory J.. Particles in Water: Properties and Processes[M], London: IWA Publishing, 2006: 137—138 [17]DUAN Xue(段雪), ZHANG Fa-Zhi(张法智). Intercalated Assembly and Functional Materials(插层组装与功能材料)[M], Beijing: Chemical Industry Press, 2007: 48—100 [18]Liu S. Y., Zhang J., Wang N., Liu W. R., Zhang C. G., Sun D. J.. Chem. Mater.[J], 2003, 15: 3240—3241 [19]Deng Y. J., Dixon J. B., White G. N.. Soil Sci. Soc. Am. J.[J], 2006, 70: 297—304 [20]ZHU Qing-Shi(朱清时). Polymer Physics(高分子物理学)[M], Beijing: Science Press, 2009: 68—79 [21]Prasad V.. Weakly Interacting Colloid Polymer Mixtures[D], Cambridge: Harvard University, 2002: 19—24 [22]Zaman A. A., Delorme N.. Rheol Acta[J], 2002, 41(5): 408—417 [23]Asakura S., Oosawa F. J.. Polym. Sci.[J], 1958, 33: 183—192 [24]Sear R. P.. Phys. Rev. Lett.[J], 2001, 86(20): 4696—4699 [25]Zhang S. D.. J. Chem. Phys.[J], 2002, 117(21): 9947—9958 [26]WANG Chen(王晨), YAN Peng(严鹏), XIAO Jin-Xin(肖进新). Chem. J. Chinese Universities(高等学校化学学报)[J], 2009, 30(10): 2012—2016 [27]Van der Kooij F. M., Vogel M., Lekkerkerker H. N. W.. Phys. Rev. E[J], 2000, 62(4): 5397—5402 [28]Baghdadi H. A., Jensen E. C., Easwar N.. Rheol. Acta[J], 2008, 47: 121—127 [29]Cho Y. H., McClements D. J.. Langmuir[J], 2009, 25(12): 6649—6657 [30]Jenkins P., Snowden M.. Adv. Colloid Interface Sci.[J], 1996, 68: 57—96 [31]Blijdenstein T. B. J., Winden A. J. M., Vliet T.. Colloids Surf., A[J], 2004, 245: 41—48 [32]Pochard I., Couchot P., Geffroy C., Foissy A., Persello J.. Rev. I. Fr. Petrol.[J], 1997, 52(2): 251—253