Preparation and Performance of Paraffin/Expanded Graphite/Graphene Composite Phase Change Heat Storage Material

doi:10.7503/cjcu20220054

Abstract

Abstract:

The paraffin/expanded graphite/graphene aerogel composite phase change material was prepared by using paraffin（PA） as the phase change heat storage material， expanded graphite（EG） as the main thermal conductive material and support material， and graphene aerogel（GA） as the thermal conductivity enhancement material and auxiliary support material. The effects of the amount of GA added on the phase transition temperature， latent heat of phase transition， thermal conductivity and cycling stability of the composite material were investigated. The results show that the phase change material with composition of 80%PA-17%EG-3%GA has good thermal conductivity and excellent cycling stability. Compared with 80%PA-20%EG composite material， it exhibits almost the same phase transition temperature， latent heat of phase transition and cycling stability， but increased thermal conductivity from 4.089 W/（m·K） to 5.336 W/（m·K）， showing good application prospects.

Key words: Phase change thermal storage material, Paraffin, Expanded graphite, Thermal conductivity enhancement, Graphene aerogel

CLC Number:

TrendMD:

YAN Jiasen, HAN Xianying, DANG Zhaohan, LI Jiangang, HE Xiangming. Preparation and Performance of Paraffin/Expanded Graphite/Graphene Composite Phase Change Heat Storage Material[J]. Chem. J. Chinese Universities, 2022, 43(6): 20220054.

Figures/Tables 9

References 32

1	Jin L.， Xie P.， Zhao Y. Q.， Zou B. Y.， Ding Y. L.， Lan Y. L.， Qiao G.， Mater. Rep.， 2021， 35（21）， 21113—21126
	金露，谢鹏，赵彦琦，邹博杨，丁玉龙，蓝元良，谯耕. 材料导报， 2021， 35（21）， 21113—21126
2	Li Z. Q.， Yang J. G.， Power Technol.， 2020， 44（9）， 1287—1292
	李泽群，杨建国. 电源技术， 2020， 44（9）， 1287—1292
3	He Y. H.， Yue X. K.， Fan R.， Zhi M. Y.， Battery， https：//kns.cnki.net/kcms/detail/43.1129.TM.20210820.0921.002.html
	贺元骅，余兴科，樊榕，智茂永. 电池， https：//kns.cnki.net/kcms/detail/43.1129.TM.20210820.0921.002.html
4	Zhou X.， South. Agr. Mach.， 2020， 51（22）， 140—141
	周璇. 南方农机， 2020， 51（22）， 140—141
5	Wang J. Q.， Sci. Technol. Inform.， 2014， 12（19）， 105
	王继强. 科技资讯， 2014， 12（19）， 105
6	Dai W.， Zhang B.， Chen L.， Metropol. Rail Transit， 2021， 34（4）， 34—38
	代伟，张斌，陈林. 都市快轨交通， 2021， 34（4）， 34—38
7	Xiong Z. H.， Liu H. T.， Commun. Power Technol.， 2014， 31（6）， 92—95
	熊振华，刘慧婷. 通信电源技术， 2014， 31（6）， 92—95
8	Liu F. F.， Bao R. Q.， Cheng X. F.， Li J.， Qin W.， Yang C. F.， Energy Storage Sci. Technol.， 2021， 10（6）， 2269—2282
	刘霏霏，鲍荣清，程贤福，李骏，秦武，杨超峰. 储能科学与技术， 2021， 10（6）， 2269—2282
9	Jin Y.， Han T.， Han X.， Kang X.， Energy Storage Sci. Technol.， 2019， 8（S1）， 23—30
	金远，韩甜，韩鑫，康鑫. 储能科学与技术， 2019， 8（S1）， 23—30
10	Lv S. Y.， Zeng W. Q.， Yang Y.， Li K. X.， New Energy Prog.， 2020， 8（6）， 493—501
	吕少茵，曾维权，杨洋，李恺翔. 新能源进展， 2020， 8（6）， 493—501
11	Zhang G. P.， Gao L.， Gui Z. X.， He B.， Geng X. W.， J. Jiamusi Univ. （Nat. Sci. Edition）， 2020， 38（4）， 99—101， 105
	张高平，高琳，桂仲喜，何博，耿学文. 佳木斯大学学报（自然科学版）， 2020， 38（4）， 99—101， 105
12	Hu D. H.， Xu X. Y.， Lin K.， Li Q.， J. Eng. Therm.， 2021， 42（9）， 2414—2418
	胡定华，许肖永，林肯，李强. 工程热物理学报， 2021， 42（9）， 2414—2418
13	Lin K.， Xu X. Y.， Li Q.， Hu D. H.， J. Chem. Ind.， 2021， 72（8）， 4425—4432
	林肯，许肖永，李强，胡定华. 化工学报， 2021， 72（8）， 4425—4432
14	Huang J. H.， Cheng Q.， Cao M.， Liu Z. Q.， Hu J.， New Chem. Mater.， 2022， 50（2）， 140—144， 149
	黄菊花，陈强，曹铭，刘自强，胡金. 化工新型材料， 2022， 50（2）， 140—144， 149
15	Xu T.， Li Y. T.， Chen J. Y.， Wu H. J.， Zhou X. Q.， Zhang Z. G.， Appl. Therm. Eng.， 2018， 40， 13—22
16	Zuo X. C.， Zhao X. G.， Li J. W.， Hu Y. Q.， Yang H. M.， Chen D. L.， Sol. Energy， 2020， 209， 85—95
17	Zhang B.， Tian Y. Y.， Jin X. Y.， Tommy Y L， Cui H. Z.， Materials， 2018， 11， 2205—2223
18	Dowan K.， Jeyoung J.， Youngno K.， Miji L.， Jongchul S.， Sher B. K.， Int. J. Heat Mass Tran.， 2016， 96， 735—741
19	Ren S.， Rong P.， Yu Q.， Jiang L. Y.， Li Y. P.， Carbon Technol.， 2019， 38（4）， 23—27
	任帅，容萍，于琦，姜立运，李亚鹏. 炭素技术， 2019， 38（4）， 23—27
20	He M. Z.， Yang L. W.， Lin W. Y.， Chen J. X.， Mao X.， Ma Z. J.， J. Energy Storage， 2019， 25， 100874
21	Zhang Y. F.， Li W.， Huang J. H.， Cao M.， Du G. P.， Materials， 2020， 13， 894—907
22	Cheng F.， Lv Z. F.， Xu Y. F.， Huang Z. H.， Min X.， Fang M. H.， Liu Y. G.， Wu X. W.， Compos. Sci. Technol.， 2020， 188， 107965
23	Zhao Y. Q.， Jin L.， Zou B. Y.， Geng Q.， Zhang T. T.， Cong L.， Jiang F.， Li C.， Huang Y.， Ding Y. L.， Appl. Therm. Eng.， 2020， 171， 115015
24	Guo X.， Zhang S. D.， Cao J. Z.， Composites： Part A， 2018， 107， 83—93
25	Guo Q.， Wang T.， Thermochim. Acta， 2015， 613， 66—70
26	Wang X. L.， Li B.， Qu Z. G.， Zhang J.F.， Jin Z.G.， Int. J. Heat Mass Tran.， 2020， 155， 119853
27	Francis A.， Neil H.， Philip E.， Mervyn S.， Renew. Sust. Energ. Rev.， 2010， 14， 615—628
28	Lachheb M.， Karkri M.， Albouchi F.， Sassi B. N.， Magali F.， Patrik S.， Composites Part B： Engineering， 2014， 66， 518—525
29	Li L.， Zhang D.， Deng J. P.， Gou Y. C.， Fang J. F.， Cui H.， Zhao Y. Q.， Cao M. H.， Carbon， 2021， 183， 721—734
30	Lui Z.， Felipe C. P.， Comp. Mater. Sci.， 2021， 196， 110493
31	Lu B. H.， Zhang Y. X.， Sun D.， Jing X. L.， Renew. Energ.， 2021， 178， 669—678
32	Bai J. G.， Yuan Z. J.， Liu Y.， Zhang Y. S.， Lv X. F.，Chem. Ind. Eng. Pro.， 2022， DOI：10.16085/j.issn.1000⁃6613.2021⁃2102
	白金刚，苑正己，刘雨，张义师，吕喜凤. 化工进展， 2022， DOI：10.16085/j.issn.1000⁃6613.2021⁃2102

Sample	m（PA）/g	m（EG）/g	m（GA）/g
E₂₀G₀	4.00	1.00	0.00
E₁₉G₁	4.00	0.95	0.05
E₁₈G₂	4.00	0.90	0.10
E₁₇G₃	4.00	0.85	0.15

Sample	m（PA）/g	m（EG）/g	m（GA）/g
E₂₀G₀	4.00	1.00	0.00
E₁₉G₁	4.00	0.95	0.05
E₁₈G₂	4.00	0.90	0.10
E₁₇G₃	4.00	0.85	0.15

[1]	ZHAO Junyu, WANG Chunbo, WANG Chengyang, ZHANG Ke, CONG Bing, YANG Lan, ZHAO Xiaogang, CHEN Chunhai. Preparation and Performance of Thermally Conductive Expanded Graphite/Polyetherimide Composites [J]. Chem. J. Chinese Universities, 2022, 43(4): 20210800.
[2]	LI Bowen,WANG Ruoheng,LI Li,XIAO Yang. Adsorption of Toluene by Alkali Activated Porous Carbons and Activation/Adsorption Mechanism ^† [J]. Chem. J. Chinese Universities, 2020, 41(2): 284.
[3]	LI Chenguang, HUA Er, LIU Tianxia. Tribological Behaviour of Protic Ionic Liquid Composed of 2-Ethylhexylethylenediaminium Cation and Trifluoromethanesulfonate Anion as Liquid Paraffin Additive^† [J]. Chem. J. Chinese Universities, 2019, 40(7): 1411.
[4]	XU Congbin, ZHANG Li, YANG Wenjie, SUN Hongliang, LIU Weijiang, JIAO Zhenhuan, JIAO Chunlei, LIN Aijun. Nitrate Removal by Expanded Graphite Loaded with Zero-valent Iron:Performance and Mechanism [J]. Chem. J. Chinese Universities, 2017, 38(8): 1415.
[5]	JIAO Chunlei, XU Congbin, LI Shuyan, YANG Wenjie, SUN Hongliang, LIU Weijiang, JIAO Zhenhuan, LIN Aijun. Preparation and Arsenic Removal Mechanism of Iron Oxyhydroxide/expanded Graphite Composite Material [J]. Chem. J. Chinese Universities, 2017, 38(8): 1316.
[6]	ZHANG Long, HOU Jieqiong, QIU Hu, DUAN Wenjing, WANG Xiaorui, WAN Xiaona, DU Xueyan. Fabrication and Microwave Absorption Performances of EG-PANI-Fe₃O₄ Composites^† [J]. Chem. J. Chinese Universities, 2017, 38(12): 2352.
[7]	WANG Huili, ZHAO Yue, MA Lekuan, FAN Penghao, XU Congbin, JIAO Chunlei, LIN Aijun. Preparation of Composite Modified Expanded Graphite and Its Adsorption on Acid Brilliant Blue Dye^† [J]. Chem. J. Chinese Universities, 2016, 37(2): 335.
[8]	LI Wa, LI Fengyun, SHI Zhisheng, HUANG Jue, CAI Qiang, ZHANG Wei. Preparation and Characterization of Strong-lightweight Porous Silica Spheres in Millimeter Scale^† [J]. Chem. J. Chinese Universities, 2015, 36(9): 1655.
[9]	ZHANG Ruizhen, WANG Cui, XING Pu, WEN Shaobo, WANG Jian, ZHAO Liangfu, LI Yuping. Preparation of Hierarchical Porous HZSM-5 and Its Application in Light Paraffin Aromatization^† [J]. Chem. J. Chinese Universities, 2015, 36(4): 725.
[10]	WEI Yingxiang, TU Weixia. Reduction of Hexavalent Chromium over the Expanded Graphite Supported Palladium Nanocatalyst^† [J]. Chem. J. Chinese Universities, 2014, 35(11): 2397.
[11]	ZHANG Qiuxiang, CHEN Jianhua, LU Hongbin, TANG Wei, LU Yu, GAO Yangzhi. Preparation and Properties of Paraffin Microencapsulated Phase-change Materials with Fine Particle Size^† [J]. Chem. J. Chinese Universities, 2014, 35(10): 2258.
[12]	XU Feng, XIANG Chen, LI Liang-Chao, MAO Meng-Yi, ZHOU Yan, DING Yan, LI Juan-Bi. Preparation and Electromagnetic Properties of CoFe₂O₄ and Its Composites with Expanded Graphite [J]. Chem. J. Chinese Universities, 2013, 34(10): 2254.
[13]	JIANG Bao-Jiang, WANG Peng-Fei, HOU Zong-Wei, QIAO Ying-Jie, FU Hong-Gang. In situ Growth of Zinc Oxide within Expended Graphite and Enhanced Photocatalytic Performance [J]. Chem. J. Chinese Universities, 2012, 33(11): 2544.
[14]	ZHANG De-Long, LI Wan-Wan, WANG Xie-Bing, SUN Kang. Preparation and Properties of High-quality CdSeS Alloyed Quantum Dots in Liquid Paraffin [J]. Chem. J. Chinese Universities, 2012, 33(07): 1383.
[15]	MENG Xin, ZHANG Huan-Zhi, ZHAO Zi-Ming, SUN Li-Xian, XU Fen, ZHANG Jian, JIAO Qing-Zhu, BAO Yan, MA Jian-Zhong. Preparation, Encapsulation and Thermal Properties of Fatty Acid/Expanded Graphite Composites as Shape-stabilized Phase Change Materials [J]. Chem. J. Chinese Universities, 2012, 33(03): 526.