接枝共聚法制备聚乙二醇(PEG)/聚乙烯醇(PVA)高分子固-固相变材料性能研究

张梅, 那莹, 姜振华   

  1. 吉林大学化学学院, 长春 130023
  • 收稿日期:2003-12-29 出版日期:2005-01-10 发布日期:2005-01-10
  • 通讯作者: 姜振华(1961年出生),男,博士,教授,博士生导师,主要从事多相高分子材料研究.E-mail:jiangzhenhua@email.jlu.cn E-mail:jiangzhenhua@email.jlu.cn
  • 基金资助:

    国家自然科学基金(批准号:50203004)资助

Preparation and Properties of Polymeric Solid-solid Phase Change Materials of Polyethylene Glycol(PEG)/Poly(vinyl alcohol)(PVA) Copolymers by Graft Copolymerization

ZHANG Mei, NA Ying, JIANG Zhen-Hua   

  1. College of Chemistry, Jilin University, Changchun 130023,China
  • Received:2003-12-29 Online:2005-01-10 Published:2005-01-10

PDF (PC)

被引次数

135

摘要： 用接枝共聚法将具有相变特征的聚乙二醇(PEG)接枝到具有较高熔点的聚乙烯醇(PVA)主链上,得到了系列性能稳定的PEG/PVA高分子固-固相转变材料,用DSC,WAXD和POM对其相变行为及形态结构进行了研究.结果表明,该材料呈现出可逆的固-固相转变特性;其结晶峰值温度和相变焓比纯PEG低,接枝率对相变温度和归一化相变焓影响不大;接枝率只影响结晶与熔融行为,不影响结晶结构.

关键词: 聚乙二醇, 聚乙烯醇, 固-固相变, 接枝共聚, 结晶

Abstract: New serials of PVA-g-PEG graft copolymers with different molecular weights and different graft ratios were prepared. In these new materials,the rigid polymer PVA served as a skeleton, and the flexible polymer PEG served as a functional branch chain. The structures of the copolymers were measured with FTIR. Their phase change properties and crystallization behavior were analyzed by DSC, POM, and WAXD. During the transition, the whole polymers remained in the solid state, they all had solid-solid phase transition properties, and the phase transitions were all reversible. Compared with pure PEG, the maximum crystalline temperatures and enthalpies of the graft copolymers declined because of the addition of PVA and the value of phase change temperatures and enthalpies had no relationship with their graft ratio. The crystalline degrees of these phase change materials were affected due to the intermolecular interaction and chemical bond.

Key words: Polyethylene glycol(PEG), Poly(vinyl alcohol)(PVA), Solid-solid phase change, Graft copolymerization, Crystallization