Pore Structure of Graphdiyne： Design， Synthesis and Application

doi:10.7503/cjcu20200663

Abstract

Abstract:

As a new emerging carbon material， graphdiyne（GDY） presents abundant sub-nanoscale porous structure， special electronic properties， and can be achieved at relatively low temperature with a wet-chemical approach. Therefore， with those excellent properties， GDY has drawn great attentions in various research fields such as catalysis， energy conversion and storage. A prominent feature of GDY is its topologically ordered regular pore structures， while the bottom-up synthesis of GDY makes it structurally designable. In the past decade， a large number of experimental and theoretical researches have been carried out on its structure design， which reveals broad application prospects. Inspired by this， we systematically summarize the effects of monomers， catalysts， templates， and solvents on GDY’s porous structures and discuss its corresponding applications. We hope it will provide a guideline for the application-oriented design and synthesis of GDY with special pore structure. Finally， the challenges and opportunities brought by the design of porous structure of GDY are discussed， and the design of three-dimensional porous structure of GDY is prospected.

Key words: Graphdiyne, Pore structure design, Three dimensional, Synthesis, Application

CLC Number:

O613

TrendMD:

ZHAN Shuhui, ZHAO Yasong, YANG Nailiang, WANG Dan. Pore Structure of Graphdiyne： Design， Synthesis and Application[J]. Chem. J. Chinese Universities, 2021, 42(2): 333.

Figures/Tables 14

Fig.1 Classification of GDY’s pore structuresMolecular pore: (A) fluorine-substituted GDY[11], Copyright 2018, RSC Publishing; (B) GDY; piled pore: (C) GDY nanowall[13], Copyright 2015, ACS Publishing; (D) GDY nanotube[14], Copyright 2011, ACS Publishing; (E) 3D hierarchical structured GDY[15], Copyright 2017, ACS Publishing; (F) 3D diatomite shaped GDY[12]， Copyright 2018, Wiley Publishing.

Fig.2 Schematics of GDY’s pore structures designThe structures can be manipulated by adjusting monomers, catalysts, templates and solvent for target-applications such as water treatment, lithium-ion batteries, catalysis, etc.

Fig.3 Application?oriented design of GDYPerformance required in the application and its corresponding structure design strategies[12,15,22—24]. Copyright 2018, Wiley Publishing; Copyright 2017, ACS Publishing; Copyright 2013, IOP Publishing; Copyright 2018, Wiley Publishing; Copyright 2019, ACS Publishing.

Table 1 Molecular pore structures and sizes of GDY prepared by different monomers

Monomer	Structure	Size(diameter)/nm	Condition	Ref.
		0.54	Copper foil, pyridine	[5]
		0.59	Copper foil, pyridine	[25]
		1.3	Copper foil, pyridine	[11]
Monomer	Structure	Size(diameter)/nm	Conditions	Ref.
		1.6	Copper foil, pyridine	[26]
		1.63	Copper foil, pyridine	[20]
		1.66	Copper foil, CH₂Cl₂, TMEDA	[17]
		1.5	Copper foil, pyridine	[27]

Fig.4 Mechanism of Glaser?Eglinton reaction(A) and Glaser?Hay reaction(B)

Fig.5 Growth of GDY on gas/liquid interface(A)[40], solid(graphene)/liquid(solvent) interface(B)[41], silver through CVD method(C)[42] and liquid/liquid interface(D)[40](A, D) Copyright 2017, ACS Publishing; (B) Copyright 2018, American Association for the Advancement of Science; (C) Copyright 2017,Wiley Publishing.

Fig.6 Structures(A—C) and pore electron density isosurfaces(D—F) of GDY?H(A, D), GDY?F(B, E) and GDY?O(C, F) monolayers[54]Gray sphere: C; white sphere: H; blue sphere: F; red sphere: O. Copyright 2017, Elsevier Publishing.

Fig.7 Structures of α?garphyne, β?garphyne and γ?garphyne(A), schematic diagram of graphyne used for seawater desalination(B), performance comparison between graphyne and commercial reverse osmosis membranes(C) and single?pore flow rates of α?garphyne, β?garphyne and graphyne?3 at different pressures(D)[22]Copyright 2013, IOP Publishing.

Fig.8 Coordination number of Cu atoms and the positions of intermediates vary with molecular different pore sizes(A) and onset potentials of the products of CO2 reduction on Cu?Graphynes(B)[60]Copyright 2020, RSC Publishing.

Fig.9 Storage sites of lithium ions in Cl?substituted GDY(gray sphere: C, green sphere: Cl, orange sphere: Li)(A), the cycling performance of Cl?substituted GDY in lithium batteries(B)[26], storage sites of lithium ion in F?substituted GDY(gray sphere: C, yellow sphere: F, purple sphere: Li)(C) and cycling performance of F?substituted GDY in lithium batteries(D)[11](A, B) Copyright 2017, Wiley Publishing; (C, D) Copyright 2018, RSC Publishing.

Fig.10 Three?dimensional GDY nanosheets on copper foil substrates prepared by a modified Glaser?Hay coupling reaction(A), the cycle performance of sodium batteries based on 3D GDY nanosheets at the current density of 1 A/g(B)[69], schematic for weaving the network of ultrathin GDY nanosheets on the Si anode(C), SEM images of ultrathin GDY nanosheets on the Si anode(D) and the performance of the as‐ prepared sample at a high current density of 2 A/g(E)[23](A, B) Copyright 2017, ACS Publishing; (C—E) Copyright 2018, Wiley Publishing.

Fig.11 3D copper nanowires@GDY(A), lithium deposited in the pores of 3D copper nanowires@GDY(B) and stability of lithium metal batteries based on 3D copper nanowires@GDY(C)[24]Copyright 2019, ACS Publishing.

Fig.13 SEM images of 3D diatomite shaped GDY(A, B), schematic illustration of 4?nitrophenol reduction catalyzed by Rh@3DGDY(C), TEM image of Rh@3DGDY(D) and time?dependent UV?Vis absorption spectra recorded during the 4?nitrophenol reduction catalyzed by Rh@3DGDY(E)[12]Copyright 2018, Wiley Publishing.

References 76

1	Zhou J. Y.， Zhang J.， Liu Z. F.， Acta Phys.⁃Chim. Sin.， 2018， 34（9）， 977—991
2	Chen M. Q.， Guan R. N.， Yang S. F.， Adv. Sci.， 2019， 6， 1800941
3	Liu L. Q.， Ma W. J.， Zhang Z.， Small， 2011， 7（11）， 1504—1520
4	Zeng M.， Wang W. L.， Bai X. D.， Chin. Phys. B， 2013， 098105
5	Li G. X.， Li Y. L.， Liu H. B.， Guo Y. B.， Li Y. J.， Zhu D. B.， Chem. Commun.， 2010， 46， 3256—3258
6	Liu M. H.， Li Y. L.， Acta Phys.⁃Chim. Sin.， 2018， 34（9）， 959—960
7	Gao X.， Liu H. B.， Wang D.， Zhang J.， Chem. Soc. Rev.， 2019， 48， 908—936
8	Janas D.， Liszka B.， Mater. Chem. Front.， 2018， 2（1）， 22—35
9	Dai L. M.， Mau A. W. H.， Adv. Mater.， 2001， 13（12/13）， 899—913
10	Yang N. L.， Zhai J.， Wang D.， Chen Y. S.， Jiang L.， ACS Nano， 2010， 4， 887—894
11	He J. J.， Wang N.， Yang Z.， Shen X. Y.， Wang K.， Huang C. S.， Yi Y. P.， Tu Z. Y.， Li Y. L.， Energy Environ. Sci.， 2018， 11， 2893—2903
12	Li J. Q.， Xu J.， Xie Z. Q.， Gao X.， Zhou J. Y.， Xiong Y.， Chen C. G.， Zhang J.， Liu Z. F.， Adv. Mater.， 2018， 30， 1800548
13	Zhou J. Y.， Gao X.， Liu R.， Xie Z. Q.， Yang J.， Zhang S. Q.， Zhang G. M.， Liu H. B.， Li Y. L.， Zhang J.， Liu Z. F.， J. Am. Chem. Soc.， 2015， 137， 7596—7599
14	Li G. X.， Li Y. L.， Qian X. M.， Liu H. B.， Lin H. W.， Chen N.， Li Y. J.， J. Phys. Chem. C， 2011， 115， 2611—2615
15	Gao X.， Ren H. Y.， Zhou J. Y.， Du R.， Yin C.， Liu R.， Peng H. L.， Tong L. M.， Liu Z. F.， Zhang J.， Chem. Mater.， 2017， 29， 5777—5781
16	Jang B.， Koo J.， Park M.， Lee H.， Nam J.， Kwon Y.， Lee H.， Appl. Phys. Lett.， 2013， 103， 263904
17	Wang F.， Zuo Z. C.， Li L.， Li K.， He F.， Jiang Z. Q.， Li Y. L.， Angew. Chem. Int. Ed.， 2019， 58， 15010—15015
18	Zhang L. Y.， Wu C.， Ding X. D.， Fang Y.， Sun J.， Phys. Chem. Chem. Phys.， 2018， 20， 18192—18199
19	Bartolomei M.， Carmona⁃Novill E.， Hernandez M. I.， Campos⁃Martinez J.， Pirani F.， Giorgi G.， J. Phys. Chem. C， 2014， 118， 29966—29972
20	He J. J.， Wang N.， Cui Z. L.， Du H. P.， Fu L.， Huang C. S.， Yang Z.， Shen X. Y.， Yi Y. P.， Tu Z. Y.， Li Y. L.， Nat. Commun.， 2017， 8， 1172
21	Yu H. D.， Xue Y. R.， Hui L.， Zhang C.， Li Y. J.， Zuo Z. C.， Zhao Y. J.， Li Z. B.， Li Y. L.， Adv. Mater.， 2018， 1707082
22	Xue M. M.， Qiu H.， Guo W. L.， Nanotechnology， 2013， 24， 505720
23	Shang H.， Zuo Z. C.， Yu L.， Wang F.， He F.， Li Y. L.， Adv. Mater.， 2018， 30， 1801459
24	Shang H.， Zuo Z. C.， Li Y. L.， ACS Appl. Mater. Interfaces， 2019， 11， 17678—17685
25	Wang N.， Li X. D.， Tu Z. Y.， Zhao F. H.， He J. J.， Guan Z. Y.， Huang C. S.， Yi Y. P.， Li Y. L.， Angew. Chem. Int. Ed.， 2018， 57， 3968—3973
26	Wang N.， He J. J.， Tu Z. Y.， Yang Z.， Zhao F. H.， Li X. D.， Huang C. S.， Wang K.， Jiu T. G.， Yi Y. P.， Li Y. L.， Angew. Chem. Int. Ed.， 2017， 56， 10740—10745
27	Shang H.， Zuo Z. C.， Zheng H. Y.， Li K.， Tu Z. Y.， Yi Y. P.， Liu H. B.， Li Y. J.， Li Y. L.， Nano Energy， 2017， 44， 144—154
28	Sonoda M.， Inaba A.， Itahashi K.， Tobe Y.， Org. Lett.， 2001， 3， 2419
29	Anthony J. E.， Khan S. I.， Rubin Y.， Tetrahedron Lett.， 1997， 38， 3499—3502
30	Shi W.， Lei A.W.， Tetrahedron Lett.， 2014， 55， 17， 2763—2772
31	Sindhu K. S.， Anilkumar G.， RSC Adv.， 2014， 4， 27867—27887
32	Si H. Y.， Deng Q. X.， Chen L. C.， Wang L.， Liu X. Y.， Wu W. S.， Zhang Y. H.， Zhou J. M.， Zhang H. L.， J. Alloys Compd.， 2019， 794， 261—267
33	Glaser C.， Ber. Dtsch. Chem. Ges.， 1869， 2， 422—424
34	Eglinton G.， Galbralth A. R.， Soc. Chemical Industry， 1956， 28， 737—738
35	Hay A. S.， J. Org. Chem.， 1962， 27（9）， 3320—3321
36	Vilhelmsen M. H.， Jensen J.， Tortzen C. G.， Nielsen M. B.， Eur. J. Org. Chem.， 2013， 701—711
37	Tang J. Y.， Jiang H. F.， Deng G. H.， Chin. J. Org. Chem.， 2005， 25， 1503
38	Gao X.， Li J.， Du R.， Zhou J. Y.， Huang M. Y.， Liu R.， Li J.， Xie Z. Q.， Wu L. Z.， Liu Z. F.， Zhang J.， Adv. Mater.， 2017， 1605308
39	Zhang S. C.， Chen Y.， Kang Z.， Wu P. W.， Wu J.， Zhang Z.， Liao Q. L.， Zhang J.， Zhang Y.， ACS Appl. Mater. Interfaces， 2019， 11， 2745—2749
40	Matsuoka R.， Sakamoto R.， Hoshiko K.， Sasaki S.， Masunaga H.， Nagashio K.， Nishihara H.， J. Am. Chem. Soc.， 2017， 139， 3145—3152
41	Gao X.， Zhu Y. H.， Yi D.， Zhou J. Y.， Zhang S. S.， Yin C.， Ding F.， Zhang S. Q.， Yi X. H.， Wang J. Z.， Tong L. M.， Han Y.， Liu Z. F.， Zhang J.， Sci. Adv.， 2018， 4（7）， eaat6378
42	Liu R.， Gao X.， Zhou J. Y.， Xu H.， Li Z. Z.， Zhang S. Q.， Xie Z. Q.， Zhang J.， Liu Z. F.， Adv. Mater.， 2017， 29， 1604665
43	Bieri M.， Nguyen M. T.， Groning O.， Cai J. M.， Treier M.， Ait⁃Mansour K.， Ruffieux P.， Pignedoli C. A.， Passerone D.， Kastler M.， Mullen K.， Fasel R.， J. Am. Chem. Soc.， 2010， 132， 16669
44	Yuan Q. H.， Ding D.， Nanoscale， 2014， 21， 12727—12731
45	Huang C. S.， Li Y. J.， Wang N.， Xue Y. R.， Zuo Z. C.， Liu H. B.， Li Y. L.， Chem. Rev.， 2018， 118（16）， 7744—7803
46	Zhang T.， Hou Y.， Dzhagan V.， Liao Z. Q.， Chai G. L.， Loffler M.， Olianas D.， Milani A.， Xu S. Q.， Tommasini M.， Zahn D. R. T.， Zheng Z. K.， Zschech E.， Jordan R.， Feng X. L.， Nat. Commun.， 2018， 9， 1140
47	van Gelderen L.， Rothenberg G.， Calderone V. R.， Wilson K.， Shiju N. R.， Appl.Organometal. Chem.， 2013， 27， 23—27
48	Zhao Y. S.， Wan J. W.， Yao H. Y.， Zhang L. J.， Lin K. F.， Wang L.， Yang N. L.， Liu D. B.， Song L.， Zhu J.， Gu L.， Liu L.， Zhao H. J.， Li Y. L.， Wang D.， Nat. Chem.， 2018， 10（9）， 924—931
49	Domyati D.， Latifi R.， Tahsini L.， J. Organomet. Chem.， 2018， 860， 98—105
50	Reichardt C.， Solvents and Solvent Effects in Organic Chemistry， Third Edition， Wiley⁃VCH Verlag GmbH & Co. KGaA， Veinheim， 2003
51	Peng J. B.， Wu X. F.， Angew. Chem. Int. Ed.， 2018， 57， 1152—1160
52	Kim S.， Gamallo P.， Vines F.， Lee J. Y.， Appl. Surf. Sci.， 2020， 499， 143927
53	Cranford S. W.， Buehler M. J.， Nanoscale， 2012， 4， 4587—4593
54	Zhao L. M.， Sang P. P.， Guo S.， Liu X. P.， Li J.， Zhu H. Y.， Guo W. Y.， Appl. Surf. Sci.， 2017， 405， 455—464
55	Xue Y. R.， Huang B. L.， Yi Y. P.， Guo Y.， Zuo Z. C.， Li Y. J.， Jia Z. Y.， Liu H. B.， Li Y. L.， Nat. Commun.， 2018， 9， 1460
56	Hui L.， Xue Y. R.， Yu H. D.， Zhang C.， Huang B. L.， Li Y. L.， ChemPhysChem， 2020， 21， 1—6
57	Zhai X. W.， Yan H. X.， Ge G. X.， Yang J. M.， Chen F.， Liu X. Y.， Yang D. Z.， Li L. F.， Zhang J. L.， Appl. Surf. Sci.， 2020， 506， 144941
58	He T. W.， Matta S. K.， Will G.， Du A. J.， Small Methods， 2019， 9， 1800419
59	Xu H. X.， Cheng D. J.， Cao D. P.， Zeng X. C.， Nat. Catal.， 2018， 1， 632—632
60	Ni Y. X.， Miao L. C.， Wang J. Q.， Liu J. X.， Yuan M. J.， Chen J.， Phys. Chem. Chem. Phys.， 2020， 22， 1181—1186
61	Xu Z. M.， Lv X.， Li J.， Chen J. G.， Liu Q. S.， RSC Adv.， 2016， 6， 25594—25600
62	Shekar S. C.， Swathi R. S.， J. Phys. Chem. A， 2013， 117， 8632—8641
63	Zhang S. L.， He J. J.， Zheng J.， Huang C. S.， Lv Q.， Wang K.， Wang N.， Lan Z. G.， J. Mater. Chem. A， 2017， 5， 2045—2051
64	Fu G. T.， Yan X. X.， Chen Y. F.， Xu L.， Sun D. M.， Lee J. M.， Tang Y. W.， Adv. Mater.， 2018， 30， 1704609
65	Zhao M. Q.， Xie X. Q.， Ren C. E.， Makaryan T.， Anasori B.， Wang G. X.， Gogotsi Y.， Adv. Mater.， 2017， 29， 1702410
66	Song H. Q.， Zhu Q.， Zheng X. J.， Chen X. G.， J. Mater. Chem. A， 2015， 3， 10368—10377
67	Qiu H. J.， Du P.， Hu K. L.， Gao J. J.， Li H. L.， Liu P.， Ina T.， Ohara K.， Ito Y.， Chen M. W.， Adv. Mater.， 2019， 31， 1900843
68	Qin J.， Wang T. S.， Liu D. Y.， Liu E. Z.， Zhao N. Q.， Shi C. S.， He F.， Ma L. Y.， He C. N.， Adv. Mater.， 2018， 30， 1704670
69	Wang K.， Wang N.， He J. J.， Yang Z.， Shen X. Y.， Huang C. S.， ACS Appl. Mater. Interfaces， 2017， 9， 40604—40613
70	Wei Y. Z.， Wang J. Y.， Yu R. B.， Wan J. W.， Wang D.， Angew. Chem. Int. Ed.，2019， 58， 1422—1426
71	Hu X. Z.， Xu W. C.， Zhou L.， Tan Y. L.， Wang Y.， Zhu S. N.， Zhu J.， Adv. Mater.， 2017， 29， 1604031
72	Qiu B. C.， Xing M. Y.， Zhang J. L.， Chem. Soc. Rev.， 2018， 47， 2165—2216
73	Gao X.， Zhou J. Y.， Du R.， Xie Z. Q.， Deng S. B.， Liu R.， Liu Z. F.， Zhang J.， Adv. Mater.， 2016， 28， 168—173
74	Liu R.， Zhou J. Y.， Li J. Q.， Xie Z. Q.， Li Z. Z.， Zhang S. Q.， Tong L. M.， Zhang J.， Liu Z. F.， Adv. Electron. Mater.， 2017， 3， 1700122
75	Yin C.， Li J. Q.， Li T. R.， Yu Y.， Kong Y.， Gao P.， Peng H. L.， Tong L. M.， Zhang J.， Adv. Funct. Mater.， 2020， 2001396
76	Yan H. L.， Yu P.， Han G. C.， Zhang Q. H.， Gu L.， Yi Y. P.， Liu H. B.， Li Y. L.， Mao L. Q.， Angew. Chem. Int. Ed.， 2018， 57， 1—6

[1]	CAO Shujie, LI Hongjun, GUAN Wenli, REN Mengtian, ZHOU Chuanzheng. Progress on the Stereocontrolled Synthesis of Phosphorothioate Oligonucleotides [J]. Chem. J. Chinese Universities, 2022, 43(Album-4): 20220304.
[2]	YAO Qing, YU Zhiyong, HUANG Xiaoqing. Progress in Synthesis and Energy-related Electrocatalysis of Single-atom Catalysts [J]. Chem. J. Chinese Universities, 2022, 43(9): 20220323.
[3]	WANG Ruyue, WEI Hehe, HUANG Kai, WU Hui. Freezing Synthesis for Single Atom Materials [J]. Chem. J. Chinese Universities, 2022, 43(9): 20220428.
[4]	WANG Xintian, LI Pan, CAO Yue, HONG Wenhao, GENG Zhongxuan, AN Zhiyang, WANG Haoyu, WANG Hua, SUN Bin, ZHU Wenlei, ZHOU Yang. Techno-economic Analysis and Industrial Application Prospects of Single-atom Materials in CO₂ Catalysis [J]. Chem. J. Chinese Universities, 2022, 43(9): 20220347.
[5]	JIN Ruiming, MU Xiaoqing, XU Yan. Bio-chemical Synthesis of Melanin Precursor—— 5，6-Dihydroxyindole（DHI） [J]. Chem. J. Chinese Universities, 2022, 43(8): 20220134.
[6]	WEI Chunhong, JIANG Qian, WANG Panpan, JIANG Chengfa, LIU Yuefeng. Atomic Scale Investigation of Pt Atoms/clusters Promoted Co-catalyzed Fischer-Tropsch Synthesis [J]. Chem. J. Chinese Universities, 2022, 43(8): 20220074.
[7]	ZHANG Xinxin, XU Di, WANG Yanqiu, HONG Xinlin, LIU Guoliang, YANG Hengquan. Effect of Mn Promoter on CuFe-based Catalysts for CO₂ Hydrogenation to Higher Alcohols [J]. Chem. J. Chinese Universities, 2022, 43(7): 20220187.
[8]	ZHOU Zixuan, YANG Haiyan, SUN Yuhan, GAO Peng. Recent Progress in Heterogeneous Catalysts for the Hydrogenation of Carbon Dioxide to Methanol [J]. Chem. J. Chinese Universities, 2022, 43(7): 20220235.
[9]	LI Yidi, TIAN Xiaochun, LI Junpeng, CHEN Lixiang, ZHAO Feng. Electron Transfer on the Semiconductor-microbe Interface and Its Environmental Application [J]. Chem. J. Chinese Universities, 2022, 43(6): 20220089.
[10]	LU Cong, LI Zhenhua, LIU Jinlu, HUA Jia, LI Guanghua, SHI Zhan, FENG Shouhua. Synthesis， Structure and Fluorescence Detection Properties of a New Lanthanide Metal-Organic Framework Material [J]. Chem. J. Chinese Universities, 2022, 43(6): 20220037.
[11]	ZHUANG Jiahao, WANG Dingsheng. Current Advances and Future Challenges of Single-atom Catalysis [J]. Chem. J. Chinese Universities, 2022, 43(5): 20220043.
[12]	WONG Honho, LU Qiuyang, SUN Mingzi, HUANG Bolong. Rational Design of Graphdiyne-based Atomic Electrocatalysts： DFT and Self-validated Machine Learning [J]. Chem. J. Chinese Universities, 2022, 43(5): 20220042.
[13]	SHA Meng, XU Weiqing, WU Zhichao, GU Wenling, ZHU Chengzhou. Recent Advances in Single-atom Materials for Enzyme-like Catalysis and Biomedical Applications [J]. Chem. J. Chinese Universities, 2022, 43(5): 20220077.
[14]	CHEN Zhaoyang, XUE Yurui, LI Yuliang. Synthesis and Applications of Graphdiyne Based Zerovalent Atomic Catalysts [J]. Chem. J. Chinese Universities, 2022, 43(5): 20220063.
[15]	FENG Li, SHAO Lanxing, LI Sijun, QUAN Wenxuan, ZHUANG Jinliang. Synthesis of Ultrathin Sm-MOF Nanosheets and Their Visible-light Induced Photodegradation of Mustard Simulant [J]. Chem. J. Chinese Universities, 2022, 43(4): 20210867.