Preparation of PANI/TiO2 Composite Nanofiber Materials by Interfacial Polymerization

Chem. J. Chinese Universities

• 研究论文 • Previous Articles Next Articles

Preparation of PANI/TiO₂ Composite Nanofiber Materials by Interfacial Polymerization

TONG Yong-Chun^1,2, HU Chang-Lin¹, WANG Qing-Yun¹, BAI Jie¹, LEI Zi-Qiang¹, SU Bi-Tao¹*

1. Key Laboratory of Eco-Environment-Related Polymer Materials, Ministry of Education, Key Laboratory of Polymer Materials of Gansu Prouince, College of Chemistry and Chemical Engineering, Northwest Normal University, Lanzhou 730070, China;
2. Department of Chemistry, Hexi University, Zhangye 734000, China

Received:2007-07-27 Revised:1900-01-01 Online:2008-02-10 Published:2008-02-10
Contact: SU Bi-Tao

Abstract

Abstract: PANI/TiO₂ composite nanofibers were successfully synthesized by interfacial polymerization(IP). TEM, FTIR, XRD and TG were used to characterize the composite materials with regard to their morphologies, structures and thermal stability. The effects of the monomer concentration and the active treatment of TiO₂ on the morphologies of the composite materials were investigated. The results show that TiO₂ nanoparticles were inserted into the nanofibers and are more homogeneously dispersed in the PANI nanofibers and the stability of PANI was improved. For the interfacial self-assemble polymerization, its conditions are mild without employing/removing template approach and the product is easy to be handled and the yield is high.

Key words: PANI/TiO₂, Composite nanofiber material, Interfacial polymerization

CLC Number:

O631.5

TrendMD:

TONG Yong-Chun^1,2, HU Chang-Lin¹, WANG Qing-Yun¹, BAI Jie¹, LEI Zi-Qiang¹, SU Bi-Tao¹*. Preparation of PANI/TiO₂ Composite Nanofiber Materials by Interfacial Polymerization[J]. Chem. J. Chinese Universities, doi: .

[1]	WANG Jiaona, YIN Zefang, LI Congju. Preparation and Desalination Performance of Composite Reverse Osmosis Membrane Based on Electrospinning Technology^† [J]. Chem. J. Chinese Universities, 2016, 37(2): 396.
[2]	LI Tao, ZHANG Long, CHEN Ying, GUO Yajun, DU Xueyan. Preparation and Electromagnetic Wave-absorbing Properties of Micro-polyaniline/Fe₃O₄ Hollow Spheres^† [J]. Chem. J. Chinese Universities, 2015, 36(4): 772.
[3]	WU Lixiang, CAI Zhibin, CHEN Xiaolin, LIU Lifen, ZHU Lifang, GAO Congjie. Stability of a Novel Poly(amide-urea-imide) Composite Reverse Osmosis Membrane^† [J]. Chem. J. Chinese Universities, 2015, 36(4): 765.
[4]	WANG Liang, DING Chun-Mei, ZHU Ying, WAN Mei-Xiang, JIANG Lei. Superhydrophobic Conducting Polyaniline Prepared via Interfacial Polymerization [J]. Chem. J. Chinese Universities, 2012, 33(06): 1355.
[5]	Lin Zhanru, Gonsalves. K.. Synthesis of Ferrocene-Containing Poiyanlides, Polyureas and Polyesters in Their Backbones by the Interfacial Technique [J]. Chem. J. Chinese Universities, 1988, 9(7): 755.

Preparation of PANI/TiO₂ Composite Nanofiber Materials by Interfacial Polymerization

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 5

Recommended Articles

Metrics

Comments