Chem. J. Chinese Universities ›› 1999, Vol. 20 ›› Issue (7): 997.
• Articles • Next Articles
XU Bin, CHENG Hu-Min, WANG Yan-Qin, MA Ji-Ming
Received:
Online:
Published:
Abstract: A new SnO2-SnS2nanosized composite particle was prepared by ion exchanging re-action. The composition, structure and size of this material were determined by XRD, TEM and X-EDAS. It′s shown that in the sample the nanosized particle SnO2was partly coated by SnS2Its average particle size was ca . 5 nm. The properties of UV-V is diffusive reflection spectrum and photoelectric chemistry were investigated. It was observed that the absorbance range of SnO2-SnS2nanosized composite particle was broadened to longer wavelength area. After being prepared to be a working electrode, its value of photocurrent and IPCEwere both highly improved, compared with pure SnO2and SnS2electrode.
Key words: SnO2-SnS2, Composite nanoparticle, Photoelectric conversion.
CLC Number:
O614
TrendMD:
XU Bin, CHENG Hu-Min, WANG Yan-Qin, MA Ji-Ming . Preparation and Photoelectric Properties of Nanosized Composite Particle SnO2-SnS2[J]. Chem. J. Chinese Universities, 1999, 20(7): 997.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: http://www.cjcu.jlu.edu.cn/EN/
http://www.cjcu.jlu.edu.cn/EN/Y1999/V20/I7/997