泡沫碳负载一维TiO2光热催化蒸发器的制备及污水蒸发降解性能

doi:10.7503/cjcu20240295

高等学校化学学报 ›› 2024, Vol. 45 ›› Issue (10): 20240295.doi: 10.7503/cjcu20240295

泡沫碳负载一维TiO₂光热催化蒸发器的制备及污水蒸发降解性能

张义东¹, 袁家相¹, 方伟¹(), 陆成龙², 陈辉¹, 何漩¹, 杜星¹, 李薇馨¹, 王大珩¹, 赵雷¹

^1.武汉科技大学省部共建耐火材料与冶金国家重点实验室，武汉 430081
^2.湖北理工学院材料科学与工程学院，黄石 435003

收稿日期:2024-06-19 出版日期:2024-10-10 发布日期:2024-08-12
通讯作者: 方伟 E-mail:fangwei@wust.edu.cn
基金资助:
国家自然科学基金(22105151);湖北省重点研发计划项目(2022BAA094);湖北省自然科学基金(2021CFB469);湖北省教育厅科学技术研究项目(B2022017);省部共建耐火材料与冶金国家重点实验室开放基金(G202407)

Preparation of Carbon Foam-loaded One-dimensional TiO₂ for Photothermal Catalytic Evaporators and Its Performances of Evaporation and Degradation for Wastewater

ZHANG Yidong¹, YUAN Jiaxiang¹, FANG Wei¹(), LU Chenglong², CHEN Hui¹, HE Xuan¹, DU Xing¹, LI Weixin¹, WANG Daheng¹, ZHAO Lei¹

^1.State Key Laboratory of Refractories and Metallurgy，Wuhan University of Science & Technology，Wuhan 430081，China
^2.School of Materials Science and Engineering，Hubei Polytechnic University，Huangshi 435003，China

Received:2024-06-19 Online:2024-10-10 Published:2024-08-12
Contact: FANG Wei E-mail:fangwei@wust.edu.cn
Supported by:
the National Natural Science Foundation of China(22105151);the Key Research Program of Hubei Province, China(2022BAA094);the Natural Science Foundation of Hubei Province, China(2021CFB469);the Scientific Research Plan of Department of Education of Hubei Province, China(B2022017);the Open Fund for the State Key Laboratory of Refractories and Metallurgy, China(G202407)

摘要/Abstract

摘要：

界面光热水蒸发是极具研究前景的有机污水纯化技术，但也存在有机污染物在光热蒸发器表面沉积的问题. 为此，本文将具有光催化效应的纳米TiO₂引入到多孔泡沫碳光热吸收体中制备了复合光热催化蒸发器（CF@RT），并对复合材料的结构和光热催化性能进行了分析. 结果表明， CF@RT中生长有大量直径约 10 nm的一维TiO₂纳米棒，纳米棒均匀分散在泡沫碳表面和孔结构中； TiO₂的引入有效拓宽了材料对光的响应范围，使复合材料具备光热和光催化双功能；多孔泡沫碳通过吸收可见-红外光转换为热能实现水的蒸发，一维TiO₂则通过吸收紫外光形成电子-空穴对，并通过氧化还原反应实现污染物降解. 同时，泡沫碳和TiO₂的结合还使光热和光催化之间存在协同促进效应，光催化过程能抑制污染物沉积，促进光热水蒸发性能持续提升，光热效应又可加速光生电子-空穴对的分离和迁移，促进光催化降解. 在太阳光照射下，最优体系CF@RT160在2.5 h内使MB降解率达到74%，光热水蒸发率为0.89 kg·m^-2·h^-1，且经4次循环后，水蒸发率提升至0.95 kg·m^-2·h^-1.

关键词: 泡沫碳, 一维TiO₂, 光热水蒸发, 光热催化

Abstract:

Interfacial photothermal water evaporation is a very promising research technique for organic wastewater purification， but there is also the problem of organic pollutant deposition on the surface of the photothermal evaporator. In this paper， composite photothermal catalytic material（CF@RT） was prepared by introducing nano-TiO₂ with photocatalytic effect into porous carbon foam photothermal absorber for simultaneous degradation of pollutants during photothermal wastewater evaporation. The structure and photothermal catalytic performance of this composite were analyzed. The results show that a large number of one-dimensional TiO₂ nanorods with a diameter of about 10 nm were grown in CF@RT， and the nanorods were homogeneously dispersed on the surface of the carbon foam and in the pore structures. The introduction of TiO₂ effectively broadens the range of the material's response to light， making the composite material dual-functional for photothermal and photocatalysis. Porous carbon foam evaporates water by absorbing visible-infrared light and converting it to heat， while one-dimensional TiO₂ absorbs UV-visible light to form electron-hole pairs and degrades pollutants through redox eactions. Meanwhile， the combination of carbon foam and TiO₂ also led to a synergistic promotional effect between photothermal and photocatalysis. The photocatalytic process inhibits pollutant deposition to promote the continuous enhancement of the evaporation performance of the photo-thermal conversion， and the photothermal effect accelerates the separation and migration of photogenerated electron-hole pairs to promote photocatalytic degradation. Under one solar irradiation， the MB degradation rate of the most effective CF@RT sample reached 74% in 2.5 h with a photothermal water evaporation rate of 0.89 kg·m^-2·h^-1. It is worth mentioning that the water evaporation of the composite evaporator has revealed a featured improvement up to 0.95 kg·m^-2·h^-1 after 4 cycles.

Key words: Carbon foam, One-dimensional TiO₂, Solar steam generation, Photothermal catalysis

中图分类号:

O643

TrendMD:

张义东, 袁家相, 方伟, 陆成龙, 陈辉, 何漩, 杜星, 李薇馨, 王大珩, 赵雷. 泡沫碳负载一维TiO₂光热催化蒸发器的制备及污水蒸发降解性能. 高等学校化学学报, 2024, 45(10): 20240295.

ZHANG Yidong, YUAN Jiaxiang, FANG Wei, LU Chenglong, CHEN Hui, HE Xuan, DU Xing, LI Weixin, WANG Daheng, ZHAO Lei. Preparation of Carbon Foam-loaded One-dimensional TiO₂ for Photothermal Catalytic Evaporators and Its Performances of Evaporation and Degradation for Wastewater. Chem. J. Chinese Universities, 2024, 45(10): 20240295.

图/表 14

Fig.1 XRD patterns(A) and Raman spectra(B) of CF and CF@RT samples

Fig.2 TG⁃DSC patterns of CF@RT140(A), CF@RT150(B) and CF@RT160(C)

Fig.3 SEM images of CF(A), CF@RT140(B), CF@RT150(C) and CF@RT160(D)

Fig.4 TEM image(A) and EDS element mapping images of C(B), O(C) and Ti(D) of CF@RT160

Fig.5 HRTEM images of CF@RT160

Fig.6 Transmittance spectra(A), reflectance spectra(B) and absorption spectra(C) of CF and CF@RT

Fig.7 Water evaporation performance of different systems(A) Real⁃time surface temperature; (B) mass loss and water evaporation rate(inset).

Fig.8 12 h dark MB adsorption rate of CF(A), CF@RT140(B), CF@RT150(C), CF@RT160(D) samples

Fig.9 UV⁃Vis absorption spectra of CF(A) and CF@RT160(B) for catalytic degradation of MB under sunlight and MB degradation activity of CF@RT photocatalytic system(C, D)

Fig.10 SEM images of CF@RT160 after reaction

Fig.11 Cyclic mass loss of CF(A) and CF@RT160(B) system, cyclic evaporation rate of CF and CF@RT160 system(C)

Fig.12 Surface temperature(A), mass change rate and water evaporation rate(inset)(B), MB photocatalytic degradation activity(C) and MB photocatalytic degradation efficiency(D) of CF@RT160 at different wavelengths

Fig.13 PL emission spectra of CF@RT160 samples at different temperatures(A), and transient fluorescence spectra corresponding to PL emission peaks(B)

Table 1 Parameters obtained by nonlinear fitting of CF@RT160 transient fluorescence spectrum

Sample	Temperature/℃	Decay time/ns		Relative amplitude（%）		Average lifetime/ns
Sample	Temperature/℃	τ₁	τ₂	A₁	A₂	Average lifetime/ns
CF@RT160	25	0.93	4.21	48.93	51.07	3.64
CF@RT160	50	1.02	5.81	46.79	53.21	5.17
CF@RT160	100	1.20	8.99	55.20	44.80	7.89

参考文献 26

1	Haddeland I.， Heinke J.， Biemans H.， Eisner S.， Flörke M.， Hanasaki N.， Konzmann M.， Ludwig F.， Masaki Y.， Schewe J.， Stacke T.， Tessler Z. D.， Wada Y.， Wisser D.， PNAS， 2014， 111（9）， 3251—3256
2	Wang Z.， Wu X.， He F.， Peng S.， Li Y.， Adv. Funct. Mater.， 2021， 31（22）， 2011114
3	Yang T.， Wang S.， Benetti D.， Wang K.， Sun Y.， Ji H.， Qian T.， Yan C.， Rosei F.， Chem. Eng. J.， 2022， 428， 131199
4	Neumann O.， Feronti C.， Neumann A. D.， Dong A.， Schell K.， Lu B.， Kim E.， Quinn M.， Thompson S.， Grady N.， Nordlander P.， Oden M.， Halas N. J.， PNAS， 2013， 110（29）， 11677—11681
5	Xu X. J.， Li B.， Lin M. X.， Zhan S.， Chem. J. Chinese Universities， 2022， 43（10）， 20220361
	许晓坚，李博，林猛枭，詹硕. 高等学校化学学报， 2022， 43（10）， 20220361
6	Yang Z. H.， Cheng H. J.， Yang Y.， Liu H.， Du F. P.， Zhang Y. F.， Chem. J. Chinese Universities， 2022， 43（10）， 20220181
	杨兆华，成鸿静，杨弋，刘辉，杜飞鹏，张云飞. 高等学校化学学报， 2022， 43（10）， 20220181
7	Tang H. Y.， Zi L. M.， Zhang B.， Fu Y.， Chem. J. Chinese Universities， 2024， 45（2）， 20230379
	唐海燕，自丽梦，张冰，付昱. 高等学校化学学报， 2024， 45（2）， 20230379
8	Yao P.， Gong H.， Wu Z. Y.， Fu H.， Li B.， Zhu B.， Ji J.， Wang X.， Xu N.， Tang C.， Zhang H.， Zhu J.， Nat. Sustainability， 2022， 5（4）， 348—356
9	Politano A.， Argurio P.， Di Profio G.， Sanna V.， Cupolillo A.， Chakraborty S.， Arafat H. A.， Curcio E.， Adv. Mater.， 2017， 29（2）， 1603504
10	Neumann O.， Urban A. S.， Day J.， Lal S.， Nordlander P.， Halas N. J.， ACS Nano， 2013， 7（1）， 42—49
11	Wang P.， Environ. Sci.： Nano， 2018， 5（5）， 1078—1089
12	Song H.， Liu Y.， Liu Z.， Singer M. H.， Li C.， Cheney A. R.， Ji D.， Zhou L.， Zhang N.， Zeng X.， Bei Z.， Yu Z.， Jiang S.， Gan Q.， Adv. Sci.， 2018， 5（8）， 1800222
13	Ghasemi H.， Ni G.， Marconnet A. M.， Loomis J.， Yerci S.， Miljkovic N.， Chen G.， Nat. Commun.， 2014， 5（1）， 4449
14	Xia Y.， Li Y.， Yuan S.， Kang Y.， Jian M.， Hou Q.， Gao L.， Wang H.， Zhang X.， J. Mater. Chem. A， 2020， 8（32）， 16212—16217
15	Liu Y.， Lou J.， Ni M.， Song C.， Wu J.， Dasgupta N. P.， Tao P.， Shang W.， Deng T.， ACS Appl. Mater. Interfaces， 2016， 8（1）， 772—779
16	Cai M.， Wu Z.， Li Z.， Wang L.， Sun W.， Tountas A. A.， Li C.， Wang S.， Feng K.， Xu A. B.， Tang S.， Tavasoli A.， Peng M.， Liu W.， Helmy A. S.， He L.， Ozin G. A.， Zhang X.， Nat. Energy， 2021， 6（8）， 807—814
17	Mu X.， Chen L.， Qu N.， Yu J.， Jiang X.， Xiao C.， Luo X.， Hasi Q.， J. Colloid Interface Sci.， 2023， 636， 291—304
18	Zhang H.， Luo W.， Du Y.， Shi H.， Zeng G.， Yan X.， Li X.， Desalination， 2023， 564， 116821
19	Nagakawa H.， Nagata M.， Adv. Mater. Interfaces， 2021， 9（2）， 2101581
20	Huang J.， He Y.， Wang L.， Huang Y.， Jiang B.， Energy Convers. Manage.， 2017， 132， 452—459
21	Wang F.， Zhao L.， Fang W.， He X.， Liang F.， Chen H.， Chen H.， Du X.， Int. J. Appl. Ceram. Technol.， 2016， 13（1）， 133—139
22	Du X.， Zhao L.， Chen H.， Qu W.， Lei Z.， Li Y.， Li S.， Colloids Surf.， A： Physicochem. Eng. Asp.， 2013， 436， 599—603
23	Chen X.， Liu L.， Yu P. Y.， Mao S. S.， Science， 2011， 331（6018）， 746—750
24	Liu X.， Cheng H.， Guo Z.， Zhan Q.， Qian J.， Wang X.， ACS Appl. Mater. Interfaces， 2018， 10（46）， 39661—39669
25	Li Y.， Shen Q.， Guan R.， Xue J.， Liu X.， Jia H.， Xu B.， Wu Y.， J. Mater. Chem. C， 2020， 8（3）， 1025—1040
26	Gu Z.， Shan Z.， Wang Y.， Wang J.， Liu T.， Li X.， Yu Z.， Su J.， Zhang G.， Chin. Chem. Lett.， 2024， 35（2）， 108356

[1]	朱佳佳, 芮家亮, 石文文, 甘铠宁, 李宏强, 何孝军. 镍/氮共掺杂自支撑泡沫碳电极的构建及电催化CO₂还原性能[J]. 高等学校化学学报, 2024, 45(10): 110.
[2]	卞宣昂, 周超, 赵运宣, 张铁锐. 基于水滑石衍生钌催化剂光驱动合成氨的研究[J]. 高等学校化学学报, 2023, 44(6): 20230095.

泡沫碳负载一维TiO₂光热催化蒸发器的制备及污水蒸发降解性能

Preparation of Carbon Foam-loaded One-dimensional TiO₂ for Photothermal Catalytic Evaporators and Its Performances of Evaporation and Degradation for Wastewater

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 14

参考文献 26

相关文章 2

编辑推荐

Metrics

本文评价