Fabrication of Highly Transparent Regular Ag Arrays

doi:10.3969/j.issn.0251-0790.2012.08.032

Abstract

Abstract: Polycaprolactam lactone(PCL) ordered porous membrane were prepared by solvent evaporation self-organization. Water drops could condenser in cold water to form regular arrays. After solvent evaporating, polymers separate and formed regular arrays on the basis of water arrays. PCL transparent films were obtained by change volume of evaporation solution. After sputtering of metal and a replacement reaction, PCL films change into Ag films. Experimental results show that the silver nets array can not only conductive than PCL array but also has higher pervious to light quality.

Key words: Self assembly, Regular Ag net array, Transparent

CLC Number:

O644
O631

TrendMD:

JIA Ruo-Kun, LIN Song-Zhu, HE Ai-Min, ZHAO Qing-Xiao, BAI Yu-Bai. Fabrication of Highly Transparent Regular Ag Arrays[J]. Chem. J. Chinese Universities, 2012, 33(08): 1809.

References

[1] Vukusic P., Sambles J. R., Lawrence C. R.. Nature[J], 2000, 404: 457 [2] Parker A. R., McPhedran R. C., McKenzie D. R., Botten L. C., Nicorovici N. A. P.. Nature[J], 2001, 409: 36-37 [3] Mohan S.. Chem. Rev.[J]. 1999, 99: 1935-1962 [4] Huang J., Wang X., Wang Z.. Nano Letters[J], 2006, 6(10): 2325-2331 [5] Wu M. H., Paul K. E., Yang J., Whitesides G. M.. Appl. Phys. Lett.[J], 2002, 80(19): 3500-3502 [6] Wu H., Odom T. W., Whitesides G. M.. Adv. Mater.[J], 2002, 14(17): 1213-1216 [7] Wu M. H., Park C., Whitesides G. M.. Langmuir[J], 2002, 18(24): 9312-9318 [8] Lopez C.. Adv. Mater.[J], 2003, 15: 1679-1704 [9] Arsenault A., Fournier-Bidoz S., Hatton B., Miguez H., Tetreault N., Vekris E., Wong S., Yang S. M., Kitaev V., Ozin G. A.. J. Mater. Chem.[J], 2004, 14: 781-794 [10] LIU Zhao-Bin(刘兆斌), ZHAO Xiang-Wei(赵祥伟), ZHANG Shuai(张帅), GU Zhong-Ze(顾忠泽). Acta Chimica Sinica(化学学报)[J], 2008, 66(2): 229-233 [11] DONG Jian( 董健 ), CAO Yue-Xia( 曹跃霞 ), QIAN Wei-Ping( 钱卫平 ). Acta Chimica Sinica( 化学学报)[J], 2006, 64(5): 388-392 [12] Stenzel M. H.. Aust. J. Chem.[J]. 2002, 55: 239-243 [13] De Boer B., Stalmach U., van Huttern P. F., Melzer C., Krasnikov V. V., Hadziioannou G.. Polymer[J], 2001, 42: 9097-9109 [14] Matsushia S. I., Kurono N., Sawadaishi T., Shimomura M.. Synthetic Metals[J], 2004, 147: 237-240 [15] Nishida J., Nishikawa K., Nishimura S. I., Wada S., Karino T., Nishikawa T., Ijiro K., Shimomura M.. Polymer Journal[J], 2002, 34: 166-174 [16] Park M. S., Kim J. K.. Langmuir[J], 2004, 20: 5347-5352 [17] Hayakawa T., Yokoyama H.. Langmuir[J], 2005, 21: 10288-10291 [18] Bormashenko E., Pogreb R., Stanevsky O., Bormashenko Y., Gendelman O.. Materials Letters[J], 2005, 59: 3553-3557 [19] Park M. S., Kin J. K.. Langmuir[J], 2005, 21: 11404-11408 [20] Erdogan B., Song L., Wilson J. N., Park J. O., Srinivasarao M., Bunz U. H. F.. J. Am. Chem. Soc. [J], 2004, 126: 3678-3679 [21] JIA Ruo-Kun(贾若琨), YAN Yong-Nan(闫永楠). Method for Preparation Amphiprotic Copolymer Poly-dodecyl Acrylic Amide Acrylic Acid(两性共聚物聚十二烷基丙烯酰胺丙烯酰酸的制备方法), CN101319027B, 2011-06-15 [22] ZHAO Feng-Hua(赵丰华), YANG Xian-Feng(杨贤锋), GAO Qiong(高琼), WU Ming-Mei(吴明娒). Chem. J. Chinese Universities(高等学校化学学报)[J], 2011, 32(3): 451-461