Abstract: Nanosize Pb3Nb2O8 powder has been obtained at 90 ℃ from Nb2O5-PbO-KOH-H2Osystem. The influence of starting materials and their molar ratios, pHvalue of the solution and the synthesis temperature were systematically investigated. Soluble niobate and lead acetate have been chosen for the synthesis of Pb3Nb2O8. Pure phase product could be obtained when the molar ratio of Pb to Nb is close to 1, and concentration of KOHto 1—3 mol/L. PbOappears as the main phase when KOHconcentration is greater than 3mol/L.
Key words: Co-deposited synthesis, Pb3Nb2O8, Nanosize powder
CLC Number:
O614.5
TrendMD:
ZHAO Hui, XIE Hong, FENG Shou-Hua . Co-deposited Synthesis of Nanosize Pb3Nb2O8 Powder[J]. Chem. J. Chinese Universities, 2001, 22(3): 355.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: http://www.cjcu.jlu.edu.cn/EN/
http://www.cjcu.jlu.edu.cn/EN/Y2001/V22/I3/355