Abstract: The intrinsic viscosities of a group of polyamidoamine PAMAM dendrimer, having ethylenediamine as the core, have been investigated. The intrinsic viscosity of G=0.5~4.5 PAMAM shows a maximum at G=2~3, while the ammonium quanternaries show a minimum there. The hydrodynamic radii of PAMAMcalculated from intrinsic viscosity, increase approximately linearly with dendrimer generation.
Key words: Polymamidoamine(PAMAM), Intrinsic viscosity, Hydrodynamic radius