Chem. J. Chinese Universities ›› 1998, Vol. 19 ›› Issue (2): 165.
• Articles • Next Articles
WANG Dan, YU Ran-Bo, FENG Shou-Hua, ZHENG Wen-Jun, PANG Guang-Sheng, ZHAO Hui
Received:
Online:
Published:
Abstract: Agiant magnetoresistance material La0.5Ba0.5MnO3 was prepared by hydrothermal method at 240 ℃ for 24 hours. The product was characterized by X-ray powder diffraction, differential thermal analysis-thermogravimetric analysis, chemical analysis, and iodometry. The compound crystallizes in a cubic system with cell parameters a =0.3913 nm and V =0.05990 nm3. The average valence state of manganese was 3.5, and the magnetoresistance (MR) is about 29% at 1 T.
Key words: La0.5 Ba0.5 MnO3, Hydrothermal systhesis, Giant magnetoresistance
CLC Number:
O611.4
TrendMD:
WANG Dan, YU Ran-Bo, FENG Shou-Hua, ZHENG Wen-Jun, PANG Guang-Sheng, ZHAO Hui. Hydrothermal Synthesis of a Giant Magnetoresistance Material La0.5Ba0.5MnO3 Under Mild Conditions[J]. Chem. J. Chinese Universities, 1998, 19(2): 165.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: http://www.cjcu.jlu.edu.cn/EN/
http://www.cjcu.jlu.edu.cn/EN/Y1998/V19/I2/165