Abstract: The double bond selective anionic polymerization of 2, 3-epoxy propyl methacrylate has been carried out.It is found that the dominant by-reaction occurred in initiation process at lower temperature(<-40℃),not in propagating period,because of the interaction between initiator and epoxy group of monomer.This by-reaction can be restricted by the use of initiator with lower reactivity.On the other hand,higher polymerization temperature(>-20℃)will result in the cross-linking reaction, so it is difficult to control the double bond selective polymerization.GPC.1HNMR and FTIR measurements indicate that a soluble functional polymer with an epoxy group in each repeating unit and monodispersity (Mw/Mn<1.10) has been prepared by proceeding the polymerization with 1,1'-diphenylhexyllithium in THF at lower temperature.
Key words: Selective anionic polymerization, Two-functionalized monomer,2,3-E-poxypropyl methacrylate, Fuflctional polymer,1 1'-Diphenylhexyl-lithium
TrendMD:
HOU Yuan-Xue, ZHANG Hong-Min. Selective Anionic Polymerization of 2,3-Epoxypropyl Methacrylate[J]. Chem. J. Chinese Universities, 1995, 16(6): 974.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: http://www.cjcu.jlu.edu.cn/EN/
http://www.cjcu.jlu.edu.cn/EN/Y1995/V16/I6/974