Synthesis， Structure， and Allochroic Property of Two Hetro-arsenomolybdates Hybrid Polyoxometalates

doi:10.7503/cjcu20210600

Abstract

Abstract:

Benzene-1，3-dicarboxylic acid（H₂BDC） and 5-hydroxy-1，3-benzene dicarboxylic acid（H₂OIP） have been employed to synthesis two organic-inorganic hybrid arsenomolybdates，（NH₄）₁₇H₄［（AsMo₆O₂₁）₂（AsMo₆O₂₃）（BDC）₄］·28H₂O（1） and （NH₄）₅Cs₈H₆［（AsMo₆O₂₁）₃（OIP）₅］·40H₂O（2）. X-Ray crystallographic study indicated that both of the two compounds are trimers. The photochromic properties have been studied. Under the irradiation of a Xe-lamp， the two compounds changed their colors within 5 min. The thermochromic study of the two compounds indicated that they changed color at 373 K， and their color deepened on the increase of temperature.

Key words: Hybrid polyoxometalate, Hetero-arsenomolybdates, Aromatic dicarboxylic acid, Photochromic property

CLC Number:

O611

TrendMD:

WANG Jin, SHI Wenjie, JIN Linyu, MA Pengtao, WANG Jingping, NIU Jingyang. Synthesis， Structure， and Allochroic Property of Two Hetro-arsenomolybdates Hybrid Polyoxometalates[J]. Chem. J. Chinese Universities, 2022, 43(1): 20210600.

Figures/Tables 7

Table 1 Crystallographic data for compounds 1 and 2

Compd.	1	2
Empirical formula	C₃₂H₁₄₄N₁₇O₁₀₉Mo₁₈As₃	C₄₀H₁₂₆N₅O₁₂₈As₃Mo₁₈Cs₈
Formula weight	4463.23	5740.31
Space group	P $1 ˉ$	P $1 ˉ$
Crystal system	Triclinic	Triclinic
a/nm	1.24069（6）	2.01214（9）
b/nm	1.83664（10）	2.03635（9）
c/nm	3.18404（17）	2.29477（11）
α/（°）	80.7030（10）	98.438（2）
β/（°）	84.4110（10）	103.434（2）
γ/（°）	85.2180（10）	107.698（2）
V/nm³	7.1092（6）	8.4694（7）
Z	2	2
D_c/（g?cm^-3）	1.794	2.088
μ/mm^-1	2.306	3.65
R_int	0.0224	0.0749
Limiting indices	-14≤h≤11	-24≤h≤24
	-19≤k≤21	-24≤k≤24
	-37≤l≤37	-27≤l≤27
Reflections collected	36733	132399
Independent reflections	25095	28855
Parameters	738	872
GOF on F²	1.013	1.164
R₁， wR₂［I>2σ（I）］	0.0788， 0.2218	0.1744， 0.3502
R₁， wR₂（all data）	0.1023， 0.2487	0.2047， 0.3680

Table 1 Crystallographic data for compounds 1 and 2

Compd.	1	2
Empirical formula	C₃₂H₁₄₄N₁₇O₁₀₉Mo₁₈As₃	C₄₀H₁₂₆N₅O₁₂₈As₃Mo₁₈Cs₈
Formula weight	4463.23	5740.31
Space group	P $1 ˉ$	P $1 ˉ$
Crystal system	Triclinic	Triclinic
a/nm	1.24069（6）	2.01214（9）
b/nm	1.83664（10）	2.03635（9）
c/nm	3.18404（17）	2.29477（11）
α/（°）	80.7030（10）	98.438（2）
β/（°）	84.4110（10）	103.434（2）
γ/（°）	85.2180（10）	107.698（2）
V/nm³	7.1092（6）	8.4694（7）
Z	2	2
D_c/（g?cm^-3）	1.794	2.088
μ/mm^-1	2.306	3.65
R_int	0.0224	0.0749
Limiting indices	-14≤h≤11	-24≤h≤24
	-19≤k≤21	-24≤k≤24
	-37≤l≤37	-27≤l≤27
Reflections collected	36733	132399
Independent reflections	25095	28855
Parameters	738	872
GOF on F²	1.013	1.164
R₁， wR₂［I>2σ（I）］	0.0788， 0.2218	0.1744， 0.3502
R₁， wR₂（all data）	0.1023， 0.2487	0.2047， 0.3680

Fig. 1 Structures of compounds 1(A) and 2(B)Color code: C, black; As, pink; MoO6 octahedral, blue.

Fig.2 Comparison of structures of arsenomolybdates and phosphomolybdates functionalized by the same carboxylic acid ligandColor code: C, black; As, pink; P, yellow; MoO6 octahedral, blue and pulm.

Fig.3 Images of compounds 1 and 2 at different times under the irradiation of a Xe lamp

Fig.4 EPR spectra of compounds 1(A) and 2(B) after light irradiation

Fig.5 Images of compounds 1 and 2 at different temperatures

Fig.6 EPR spectra of compounds 1(A) and 2(B) after heating

References 28

1	Gouzerh P.， Proust A.， Chem. Rev.， 1998， 98， 77—111
2	Weinstock I. A.， Schreiber R. E.， Neumann R.， Chem. Rev.，2018， 118， 2680—2717
3	Bijelic A.， Aureliano M.， Rompel A.， Chem. Commun.， 2018， 54， 1153—1169
4	Jin L.， Fang Y.， Hu P.， Zhai Y.， Wang E.， Dong S.， Chem. Commun.， 2012， 48， 2101—2103
5	He T.， Yao J.， Prog. Mater. Sci. 2006， 51， 810—879（何涛，姚建年. 材料科学进展， 2006， 51， 810—879）
6	Clemente⁃Juan J. M.， Coronado E.， Coord. Chem. Rev.，1999， 193—195
7	Ma P. T.， Hu F.， Wang J. P.， Niu J. Y.， Coord. Chem. Rev.， 2018， 378， 281—309
8	Chen Z.， An H.， Zhang H.， Hu Y.， CrystEngComm， 2013， 15， 4711—4720
9	Banerjee A.， Bassil B. S.， Röschenthaler G. V.， Kortz U.， Chem. Soc. Rev.， 2012， 41（22）， 7590—7604
10	Dolbecq A.， Dumas E.， Mayer C. R.， Mialane P.， Chem. Rev.， 2010， 110（10）， 6009—6048
11	May N.， Burns P. C.， Chem. Soc. Rev.， 2012， 41（22）， 7354—7367
12	Dolbecq A.， Mialane P.， Sécheresse F.， Keita B.， Nadjo L.， Chem. Commun.， 2012， 48， 8299—8316
13	Modec B.， BrenčičJ. V.， Burkholder E. M.， Zubieta J.， Dalton Trans.， 2003， 24， 4618—4625
14	Hofmann C.， Thurston J. H.， Hartman K. B.， Alemany L. B.， Whitmire K. H.， Inorg. Chim. Acta， 2009， 362， 1665—1671
15	Müller A.， Krickemeyer E.， Bögge H.， Schmidtmann M.， Peters F.， Angew. Chem.， Int. Ed.， 1998， 37， 319—328
16	Müller A.， Das S. K.， Kuhlmann C.， Bögge H.， Schmidtmann M.， Diemann E.， Krickemeyer E.， Hormes J.， Modrow H.， Schindler M.， Chem. Commun.， 2001，（7）， 655—656
17	Cindrić M.， Strukan N.， Devčić M.， Kamenar B.， Inorg. Chem. Commun.， 1999， 2， 558—560
18	Kortz U.， Savelieff M. G.， Abou Ghali F. Y.， Khalil L. M.， Maalouf S. A.， Sinno D. I.， Angew. Chem.， Int. Ed.， 2002， 41， 4070—4072
19	Kortz U.， Vaissermann J.， Thouvenot R.， Gouzerh P.， Inorg. Chem.， 2003， 42， 1135—1139
20	Liang Y.， Li S.， Yang D.， Ma P.， Niu J.， Wang J.， J. Mater. Chem. C， 2015， 3， 4632—4639
21	Wang J.， Liang Y.， Ma P.， Zhang D.， Niu J.， Wang J.， Cryst. Eng. Comm.， 2017， 19， 207—213
22	Sheldrick G. M.， Acta Cryst. A， 2008， 64， 112—122
23	Wang J.， Shi W.， Li S.， Mao Q.， Ma P.， Niu J.， Wang J.， Dalton Trans.， 2018， 47， 7949—7955
24	Yang D.， Li S.， Ma P.， Wang J.， Niu J.， Inorg. Chem.， 2013， 52， 8987—8992
25	Yang D.， Liang Y.， Ma P.， Li S.， Wang J.， Niu J.， Inorg. Chem.， 2014， 53， 3048—3053
26	Yamase T.， Chem. Rev.， 1998， 98， 307—326
27	Taylor O. K.， J. Am. Chem. Soc.， 1982， 104， 5063—5070
28	McCarron E. M. III， Harlow R. L. I.， J. Am. Chem. Soc.， 1983， 105， 6179—6181