Reconstructed Synthetic and Characterization of a Insoluble Polyoxometalate Coordination Polymer

WANG Li*, CAI Wei, OU Guang-Nan   

  1. College of Bioengineering, Jimei University, Xiamen 361021, China
  • Received:2008-12-16 Online:2009-11-10 Published:2009-11-10
  • Contact: WANG Li. E-mail： wanglimerry@jmu.edu.cn
  • Supported by:

    国家自然科学基金(批准号： 20871054)、福建省教育厅基金(批准号: 2007F5076)和福建省自然科学基金高校专项基金(批准号: 2007J0369)资助.

PDF (PC)

被引次数

6

摘要：

利用电沉积法将不溶于常规无机和有机溶剂的多金属氧酸盐基的配位聚合物1, [{La(H2O)5·(dipic)}{La(H2O)(dipic)}]2{Mo8O26}·10H2O溶解于离子液体[RMIM][HT]或[RMIM][HP]中, 在恒电位下电解, 得到多金属氧酸盐基的配位聚合物膜. 应用红外光谱、X射线光电子能谱和XRD粉末衍射等方法研究多金属氧酸盐基配位聚合物膜的结构, 发现其与多金属氧酸盐基配位聚合物有相同的结构. 实现了多金属氧酸盐基配位聚合物在电极上的重构设计以及多金属氧酸盐基的配位聚合物的二次加工成型.

关键词: 多金属氧酸盐; 离子液体; 电沉积

Abstract:

A general reconstructed synthetic strategy for ionic liquids-supported the insoluble polyoxometalate coordination polymer was proposed. A insoluble polyoxometalate(POMs) coordination polymer 1, [{La(H2O)5(dipic)}{La(H2O)(dipic)}]2{Mo8O26}·10H2O was successfully reconstructed by electrolyzing in ionic liquids on conducting glasses coated with indium tin oxide(ITO) electrode. The polyoxometalate coordination polymer is insoluble in aqueous solution and usual organic solutions, but soluble in the ionic liquid [RMIM][HT] or [RMIM][HP]. The reconstructed synthetic polyoxometalate coordination polymer was characterized via XPS and XRD techniques. The result show the XRD pattern of the deposited POMs on ITO electrode has the same crystal structure as the polyoxometalate coordination polymer 1, which imply that the crystal structure of the deposited POMs on ITO electrode keeps the same as the original POMs compound. It was favored the compound 1 reconstructed by the electrolyzing in an ionic liquid.

Key words: Polyoxometalate; Ionic liquid; Electrolyzing