Chem. J. Chinese Universities ›› 2019, Vol. 40 ›› Issue (6): 1103.doi: 10.7503/cjcu20180627
• Review • Previous Articles Next Articles
HUANG Zhiyu1, CHEN Honghui1, MA Wenle1, HUANG Yi1(), ZHU Dan2, CHEN Yongsheng1
Received:
2018-09-11
Online:
2019-06-10
Published:
2019-04-04
Supported by:
CLC Number:
TrendMD:
HUANG Zhiyu, CHEN Honghui, MA Wenle, HUANG Yi, ZHU Dan, CHEN Yongsheng. Research Progress on Terahertz Stealth and Shielding Materials†[J]. Chem. J. Chinese Universities, 2019, 40(6): 1103.
Fig.3 Structures and terahertz stealth performance of GaAs/PI metamaterials(A,B)[11] and Si/SiO2 metamaterials with dielectric thickness from 0.4 μm to 1.2 μm(C,D)[12] (A, B) Copyright 2008, Optical Society of America; (C, D) copyright 2012, American Institute of Physics.
Fig.4 Structures and terahertz stealth performance of polarization insensitivity stealth metamaterials(A,B)[18] and wide-angle stealth metamaterials(C—E)[19] (A, B) Copyright 2009, American Physical Society; (C—E) copyright 2008, American Physical Society.
Fig.8 Terahertz reflectivity of graphene at different incident angles[23] Incident angle: (A) 15°; (B) 30°; (C) 45°; (D) 60°. Copyright 2016, Elsevier.
Materials | Measured band/THz | SATAP*/ (dB·g-1·cm3) | Maxim absorption/dB | Qualified bandwidth(%) | Reference |
---|---|---|---|---|---|
Graphene foam | 0.1—1.2 | 2.37×104 | 28.6 | 100 | [ |
Terahertz metamaterial | 0.1—3.0 | 6.81 | 14 | 44.83 | [ |
Terahertz metamaterial | 0.2—2.2 | 6.31 | 15.2 | 65 | [ |
Multi-layer terahertz metamaterial | 0.2—1.6 | 5.20 | 17 | 50 | [ |
Metamaterial absorber | 1.0—10.0 | 4.76 | 17 | 22.22 | [ |
PMMA/Graphite | 0.1—1.6 | 4.37 | 13 | 13.33 | [ |
Graphene metamaterial | 0—2.5 | 3.72 | 27 | 18 | [ |
Metamaterial absorber | 0.5—2.5 | 1.39 | 5.2 | N/A | [ |
SiO2/Al based metamaterial | 2.5—6.0 | 0.96 | 17 | 5.71 | [ |
Dual-band metamaterial | 0.3—3.5 | 0.94 | 15.2 | 3.75 | [ |
Multi-band metamaterial | 0.2—2.6 | 0.85 | 17 | 2.08 | [ |
Metal/graphene plasmons | 0—10.0 | 0.67 | 3 | N/A | [ |
BaTiO3/PMMA | 0.2—0.6 | N/A | 17 | 35 | [ |
Kapton-derived carbon | 0.3—0.5 | N/A | 2.8 | N/A | [ |
Graphene-based metamaterial absorbers | 1—4.5 | N/A | 15.2 | 71.43 | [ |
Terahertz metamaterial absorber | 1.0—7.0 | N/A | 14 | 13 | [ |
Terahertz metamaterial | 1.0—3.4 | N/A | 15.2 | 4.17 | [ |
Table 1 Terahertz stealth materials reported in open literatures
Materials | Measured band/THz | SATAP*/ (dB·g-1·cm3) | Maxim absorption/dB | Qualified bandwidth(%) | Reference |
---|---|---|---|---|---|
Graphene foam | 0.1—1.2 | 2.37×104 | 28.6 | 100 | [ |
Terahertz metamaterial | 0.1—3.0 | 6.81 | 14 | 44.83 | [ |
Terahertz metamaterial | 0.2—2.2 | 6.31 | 15.2 | 65 | [ |
Multi-layer terahertz metamaterial | 0.2—1.6 | 5.20 | 17 | 50 | [ |
Metamaterial absorber | 1.0—10.0 | 4.76 | 17 | 22.22 | [ |
PMMA/Graphite | 0.1—1.6 | 4.37 | 13 | 13.33 | [ |
Graphene metamaterial | 0—2.5 | 3.72 | 27 | 18 | [ |
Metamaterial absorber | 0.5—2.5 | 1.39 | 5.2 | N/A | [ |
SiO2/Al based metamaterial | 2.5—6.0 | 0.96 | 17 | 5.71 | [ |
Dual-band metamaterial | 0.3—3.5 | 0.94 | 15.2 | 3.75 | [ |
Multi-band metamaterial | 0.2—2.6 | 0.85 | 17 | 2.08 | [ |
Metal/graphene plasmons | 0—10.0 | 0.67 | 3 | N/A | [ |
BaTiO3/PMMA | 0.2—0.6 | N/A | 17 | 35 | [ |
Kapton-derived carbon | 0.3—0.5 | N/A | 2.8 | N/A | [ |
Graphene-based metamaterial absorbers | 1—4.5 | N/A | 15.2 | 71.43 | [ |
Terahertz metamaterial absorber | 1.0—7.0 | N/A | 14 | 13 | [ |
Terahertz metamaterial | 1.0—3.4 | N/A | 15.2 | 4.17 | [ |
Sample | Reflectance | Sample | Reflectance |
---|---|---|---|
380 μm Si(polished) | 0.30 | 150 μm VANTA | 0.18 |
40 μm VANTA | 0.46 | 1.5 μm VANTA | 0.01 |
Table 2 Summary of reflectance-measurement results at 394 μm wavelength[39]
Sample | Reflectance | Sample | Reflectance |
---|---|---|---|
380 μm Si(polished) | 0.30 | 150 μm VANTA | 0.18 |
40 μm VANTA | 0.46 | 1.5 μm VANTA | 0.01 |
Fig.12 Terahertz shielding performance CNF composites with different CNF content(A)[46] and different thicknesses(B)[47] at 0.57—0.63 THz (A) Copyright 2011, American Institute of Physics; (B) copyright 2012, American Institute of Physics.
Fig.13 Transmission performance of GO with different annealing temperatures(A) and thicknesses(B) at 0.2—1.0 THz[48] Copyright 2015, Royal Society of Chemistry.
Fig.15 3D representations of the EMI SE values of MGF-1500(2∶1)(A) and the simulated RL values of MGF(2∶1) with the same thickness of 2 mm and different annealing temperatures(B)[62] Copyright 2018, American Institute of Physics.
Material | Measured band/THz | SATSCa/ (dB· g-1·cm3) | Maximum shielding effectiveness/dB | Qualifid bandwidth(%) | Reference |
---|---|---|---|---|---|
Kapton-derived carbon | 0.22—0.5 | 54.5 | 90 | 100 | [ |
Graphite/PMMA | 0.1—1.6 | 42.4 | 50 | 100 | [ |
PAN/TPU | 0.2—1.2 | 38.2 | 58 | 100 | [ |
CNW/PMC | 0.57—0.63 | 36.4 | 48 | 100 | [ |
SWCNTs | 0.2—2.5 | 29.2 | 38 | 100 | [ |
CNF/PTFE/PVDF/PMMA | 0.57—0.63 | 25.4 | 32 | 100 | [ |
OLC/KBr | 12—230 | 17.8 | 40 | 100 | [ |
MWCNTs/PMMA | 0.1—4 | 16.9 | 40 | 83 | [ |
SWCNTs/PVA | 0.3—2.1 | 15.7 | 30 | 89 | [ |
MWCNTs | 0.4—2.2 | 13.9 | 30 | 100 | [ |
Graphene/SiO2 | 0.01—100 | 13.6 | 60 | 10 | [ |
DND/KBr | 110—230 | 8.9 | 20 | 100 | [ |
SWCNTs/PET | 0.1—1.2 | 3.6 | 4 | 0 | [ |
OLC/PMMA | 0.1—3 | 3.4 | 14 | 17 | [ |
RGO | 0.3—1.0 | 0.48 | 3.8 | N/Ab | [ |
Few-layer graphene | 0.6—600 | N/Ab | 0.9 | N/Ab | [ |
Epitaxial graphene on SiC | 1.5—750 | N/Ab | 2.2 | N/Ab | [ |
Monolayer graphene | 0.57—0.63 | N/Ab | 1 | N/Ab | [ |
Graphene insulator stacks | 0.03—10.2 | N/Ab | 16 | 25 | [ |
Table 3 Terahertz shielding materials reported in open literatures
Material | Measured band/THz | SATSCa/ (dB· g-1·cm3) | Maximum shielding effectiveness/dB | Qualifid bandwidth(%) | Reference |
---|---|---|---|---|---|
Kapton-derived carbon | 0.22—0.5 | 54.5 | 90 | 100 | [ |
Graphite/PMMA | 0.1—1.6 | 42.4 | 50 | 100 | [ |
PAN/TPU | 0.2—1.2 | 38.2 | 58 | 100 | [ |
CNW/PMC | 0.57—0.63 | 36.4 | 48 | 100 | [ |
SWCNTs | 0.2—2.5 | 29.2 | 38 | 100 | [ |
CNF/PTFE/PVDF/PMMA | 0.57—0.63 | 25.4 | 32 | 100 | [ |
OLC/KBr | 12—230 | 17.8 | 40 | 100 | [ |
MWCNTs/PMMA | 0.1—4 | 16.9 | 40 | 83 | [ |
SWCNTs/PVA | 0.3—2.1 | 15.7 | 30 | 89 | [ |
MWCNTs | 0.4—2.2 | 13.9 | 30 | 100 | [ |
Graphene/SiO2 | 0.01—100 | 13.6 | 60 | 10 | [ |
DND/KBr | 110—230 | 8.9 | 20 | 100 | [ |
SWCNTs/PET | 0.1—1.2 | 3.6 | 4 | 0 | [ |
OLC/PMMA | 0.1—3 | 3.4 | 14 | 17 | [ |
RGO | 0.3—1.0 | 0.48 | 3.8 | N/Ab | [ |
Few-layer graphene | 0.6—600 | N/Ab | 0.9 | N/Ab | [ |
Epitaxial graphene on SiC | 1.5—750 | N/Ab | 2.2 | N/Ab | [ |
Monolayer graphene | 0.57—0.63 | N/Ab | 1 | N/Ab | [ |
Graphene insulator stacks | 0.03—10.2 | N/Ab | 16 | 25 | [ |
[19] | Tao H., Bingham C. M., Strikwerda A. C., Pilon D., Shrekenhamer D., Landy N. I., Fan K., Zhang X., Padilla W. J., Averitt R. D., Phys. Rev.B.,2008, 78(24), 241103 |
[20] | Jeon T. I., Son J. H., An K. H., Lee Y. H., Lee Y. S., J. Appl.Phys.,2005, 98(3), 034316 |
[21] | Seo M. A., Lee J. W., Kim D. S., J. Appl.Phys.,2006, 99(6), 066103 |
[22] | Chamorro-Posada P., Vazquez-Cabo J., Rubinos-Lopez O., Martin-Gil J., Hernandez-Navarro S., Martin-Ramos P., Sanchez-Arevalo F. M., Tamashausky A. V., Merino-Sanchez C., Dante R. C., Carbon,2016, 98, 484-490 |
[23] | Venkatachalam S., Bertin D., Ducournau G., Lampin J. F., Hourlier D., Carbon,2016, 100, 158-164 |
[24] | Zhou Y. E. Y., Zhu L., Qi M., Xu X., Eai J., Ren Z., Wang L., Carbon,2016, 96, 1129-1137 |
[25] | Zhang Y., Huang Y., Zhang T., Chang H., Xiao P., Chen H., Huang Z., Chen Y., Adv.Mater.,2015, 27(12), 2049-2053 |
[26] | Li Y., Liu X., Nie X., Yang W., Wang Y., Yu R., Shui J., Adv. Funct.Mater.,2018, 48(2), 1807624 |
[27] | Huang Z., Chen H., Huang Y., Ge Z., Zhou Y., Yang Y., Xiao P., Liang J., Zhang T., Shi Q., Li G., Chen Y., Adv. Funct.Mater.,2018, 28(2), 1704363 |
[28] | Shi C., Zang X., Wang Y., Chen L., Cai B., Zhu Y., Appl. Phys.Lett.,2014, 105(3), 031104 |
[29] | Liu S., Chen H., Cui T. J., Appl. Phys.Lett.,2015, 106(15), 151601 |
[30] | Lv J., Yuan R. Y., Song X., Yan H., J. Appl.Phys.,2015, 117(1), 013101 |
[31] | Gao R. M., Xu Z. C., Ding C. F., Ya J. Q., Appl.Opt.,2016, 55(8), 1929-1933 |
[32] | Wen Y., Ma W., Bailey J., Matmon G., Yu X., Aeppli G., Appl.Opt.,2013, 52(19), 4536-4540 |
[33] | Chen X., Fan W., Appl.Opt.,2015, 54(9), 2376-2382 |
[34] | Jadidi M. M., Sushkov A. B., Myers-Ward R. L., Boyd A. K., Daniels K. M., Gaskill D. K., Fuhrer M. S., Drew H. D., Murphy T. E., Nano Lett.,2015, 15(10), 7099-7104 |
[35] | Lott J., Xia C., Kosnosky L., Weder C., Shan J., Adv.Mater.,2008, 20(19), 3649-3653 |
[36] | He S., Chen T., IEEE Trans. Terahertz Sci. Technol.,2013, 3(6), 757-763 |
[37] | Macutkevic J., Adomavicius R., Krotkus A., Seliuta D., Valusis G., Maksimenko S., Kuzhir P., Batrakov K., Kuznetsov V., Moseenkov S., Shenderova O., Okotrub A. V., Langlet R., Lambin P., Diam. Relat.Mater.,2008, 17(7—10), 1608-1612 |
[38] | Shenderova O., Grishko V., Cunningham G., Moseenkov S., McGuire G., Kuznetsov V., Diam. Relat.Mater.2008, 17(4/5), 462-466 |
[39] | Lehman J. H., Lee B., Grossman E. N., Appl.Opt.,2011, 50(21), 4099-4104 |
[40] | Jeon T. I., Kim K. J., Kang C., Maeng I. H., Son J. H., An K. H., Lee J. Y., Lee Y. H., J. Appl.Phys.,2004, 95(10), 5736-5740 |
[1] | Kohler R., Tredicucci A., Beltram F., Beere H. E., Linfield E. H., Davies A. G., Ritchie D. A., Iotti R. C., Rossi F., Nature,2002, 417(6885), 156-159 |
[2] | Planken P. C. M., Nienhuys H. K., Bakker H. J., Wenckebach T., J. Opt. Soc. Am. B,2001, 18(3), 313-317 |
[41] | Seo M. A., Yim J. H., Ahn Y. H., Appl. Phys.Lett.,2008, 93(23), 231905 |
[42] | Hong J. T., Park D. J., Moon J. Y., Choi S. B., Park J. K., Rotermund F., Park J. Y., Lee S., Ahn Y. H., Appl. Phys.Express,2012, 5(1), 015102 |
[3] | Nagatsuma T., IEICE Electron. Expr., 2011, 8(14), 1127-1142 |
[4] | McMillan R. W., Trussell C. W., Bohlander R. A., Butterworth J. C., Forsythe R. E., IEEE Trans. Microwave Theory,1991, 39, 555-562 |
[43] | Macutkevic J., Seliuta D., Valusis G., Adomavicius R., Krotkus A., Kuzhir P., Paddubskaya A., Maksimenko S., Kuznetsov V., Mazov I., Simonova I., Diam. Relat.Mater.,2012, 25, 13-18 |
[44] | Polley D., Barman A., Mitra R. K., Opt.Lett.,2014, 39(6), 1541-1544 |
[5] | Liang D. C., Gu J. Q., Han J. G., Tian Z., Ouyang C. M., He M. X., Zhang W. L., Space Electronic Technology,2013, 10(4),99-103 |
梁达川,谷建强,韩家广,田震,欧阳春梅,何明霞,张伟力.空间电子技术, 2013, 10(4), 99-103) | |
[45] | Polley D., Neeraj K., Barman A., Mitra R. K., J. Opt. Soc. Am. B,2016, 33(12), 2430-2436 |
[46] | Das A., Megaridis C. M., Liu L., Wang T., Biswas A., Appl. Phys.Lett.,2011, 98(17), 174101 |
[6] | Hirata A., Takahashi H., Yamaguchi R., Kosugi T., Murata K., Nagatsuma T., Kukutsu N., Kado Y., J. Lightwave Technol.,2008, 26(13—16), 2338-2344 |
[7] | Rothbart N., Richter H., Wienold M., Schrottke L., Grahn H. T., Huebers H. W., IEEE Trans. Terahertz Sci. Technol.,2013, 3(5), 617-624 |
[47] | Das A., Schutzius T. M., Megaridis C. M., Subhechha S., Wang T., Liu L., Appl. Phys.Lett.,2012, 101(24), 243108 |
[48] | Zhou Y. E. Y., Ren Z., Fan H., Xu X., Zheng X., Lei D. Y., Li W., Wang L., Bai J., J. Mater. Chem.C,2015, 3(11), 2548-2556 |
[8] | Shen Y. C., Lo T., Taday P. F., Cole B. E., Tribe W. R., Kemp M. C., Appl. Phys.Lett.,2005, 86(24), 241116 |
[9] | Liu L., Das A., Megaridis C. M., Carbon,2014, 69, 1-16 |
[49] | Dawlaty J. M., Shivaraman S., Strait J., George P., Chandrashekhar M., Rana F., Spencer M. G., Veksler D., Chen Y., Appl. Phys.Lett.,2008, 93(13), 131905 |
[50] | Choi H., Borondics F., Siegel D. A., Zhou S. Y., Martin M. C., Lanzara A., Kaindl R. A., Appl. Phys.Lett.,2009, 94(17), 172102 |
[10] | Landy N. I., Sajuyigbe S., Mock J. J., Smith D. R., Padilla W. J., Phys.Rev.Lett.,2008, 100(20), 207402 |
[11] | Tao H., Landy N. I., Bingham C. M., Zhang X., Averitt R. D., Padilla W. J., Opt.Express,2008, 16(10), 7181-7188 |
[51] | Sensale-Rodriguez B., Yan R., Kelly M. M., Fang T., Tahy K., Hwang W. S., Jena D., Liu L., Xing H. G., Nat.Commun.,2012, 3, 780 |
[52] | Yan H., Li X., Chandra B., Tulevski G., Wu Y., Freitag M., Zhu W., Avouris P., Xia F., Nat.Nanotechnol.,2012, 7(5), 330-334 |
[12] | Alves F., Kearney B., Grbovic D., Lavrik N. V., Karunasiri G., Appl. Phys.Lett.,2012, 100(11), 111104 |
[13] | Huang L., Chowdhury D. R., Ramani S., Reiten M. T., Luo S. N., Taylor A. J., Chen H. T., Opt.Lett.,2012, 37(2), 154-156 |
[53] | D'Aloia A. G., D'Amore M., Sarto M. S., IEEE Trans. Terahertz Sci. Technol.,2015, 5(4), 628-636 |
[54] | Deng Y., Sun Q., Yu J., Lin Y., Wang J., Opt. Express,2013, 21(5), 5737-5742 |
[14] | Shen X., Yang Y., Zang Y., Gu J., Han J., Zhang W., Cui T. J., Appl. Phys.Lett.,2012, 101(15), 154102 |
[15] | Zhu J., Ma Z., Sun W., Ding F., He Q., Zhou L., Ma Y., Appl. Phys.Lett.,2014, 105(2), 021102 |
[55] | Batrakov K., Kuzhir P., Maksimenko S., Volynets N., Voronovich S., Paddubskaya A., Valusis G., Kaplas T., Svirko Y., Lambin P., Appl. Phys.Lett.,2016, 108(12), 123101 |
[56] | Agnandji E. N., Vigneras V., Miane J. L., Mounaix P., Electron.Lett.,2007, 43(23), 1271-1273 |
[57] | Wen B., Cao M., Hou Z., Song W., Zhang L., Lu M., Jin H., Fang X., Wang W., Yuan J., Carbon,2013, 65(2), 124-139 |
[58] | Wen B., Cao M., Lu M., Cao W., Shi H., Liu J., Wang X., Jin H., Fang X., Wang W., Yuan J., Adv.Mater.,2014, 26(21), 3484-3489 |
[16] | Wen Q. Y., Zhang H. W., Xie Y. S., Yang Q. H., Liu Y. L., Appl. Phys.Lett.,2009, 95(24), 241111 |
[17] | Wen Y., Ma W., Bailey J., Matmon G., IEEE Trans. Terahertz Sci. Technol.,2015, 5(3), 406-411 |
[59] | Cao W., Wang X., Yuan J., Wang W., Cao M., J. Mater. Chem.C,2015, 3(38), 10017-10022 |
[60] | Cao M., Wang X., Cao W., Fang X., Wen B., Yuan J., Small,2018, 14(29), 1800987 |
[61] | Choi G., Shahzad F., Bahk Y., Jhon Y., Park H., Alhabeb M., Anasori B., Kim D., Koo C., Gogotsi Y., Adv. Opt.Mater.,2018, 6(5), 1701076 |
[62] | Huang Z., Chen H., Xu S., Chen L. Y., Huang Y., Ge Z., Ma W., Liang J., Fan F., Chang S., Chen Y., Adv. Opt.Mater.,2018, 6(23), 1801165 |
[18] | Landy N. I., Bingham C. M., Tyler T., Jokerst N., Smith D. R., Padilla W. J., Phys. Rev.B.,2009, 79(12), 125104 |
[63] | Oh K., Hong S. M., Seo Y., Polym. Adv.Technol.,2014, 25(11), 1366-1370 |
[64] | Gelves G. A., Lin B., Sundararaj U., Haber J. A., Adv. Funct.Mater.,2006, 16(18), 2423-2430 |
[65] | Al-Saleh M. H., Gelves G. A., Sundararaj U., Compos. Part A: Appl. S,2011, 42(1), 92-97 |
[66] | Yang Y. L., Gupta M. C., Dudley K. L., Lawrence R. W., Adv.Mater.,2005, 17(16), 1999-2003 |
[67] | Al-Saleh M. H., Sundararaj U., Carbon,2009, 47(7), 1738-1746 |
[68] | Zhang H. B., Yan Q., Zheng W. G., He Z., Yu Z. Z., ACS Appl. Mater.Inter.,2011, 3(3), 918-924 |
[1] | LÜ Tong,ZHANG Enshuang,YUAN Yin,FAN Zhimin,MA Xiangyu,CHENG Zhongjun,LIU Yuyan,GONG Yuanxun,ZHAO Hongjie. Preparation of Large-size Single Layer MXene with Low Defect and Electromagnetic Shielding Performance of MXene Film [J]. Chem. J. Chinese Universities, 2019, 40(10): 2059. |
[2] | FANG Hongxia, ZHANG Qi, ZHANG Huili, QIN Dan, HONG Zhi, DU Yong. Terahertz Spectroscopic and Density Functional Theoretical Analysis of Cocrystal Between Olmesartan and Benzoic Acid† [J]. Chem. J. Chinese Universities, 2015, 36(12): 2504. |
[3] | CHEN Ran, AN Zhongwei, CHEN Xinbing, CHEN Pei. Syntheses and Properties of Four-ring Liquid Crystals with Ethylene and Internal Alkyne Bridge† [J]. Chem. J. Chinese Universities, 2014, 35(7): 1433. |
Viewed | ||||||
Full text |
|
|||||
Abstract |
|
|||||