Growth of ZnO Film by Plasma-assisted MOCVD

Abstract

Abstract: The growth of ZnO film by plasma-assisted MOCVD was reported in this atricle.From X-ray diffraction spectrum, the intensity of (0002) peak at 2θ=34.56°was high, indicating a c-axis orientation perpendicular to the substrate surface in ZnO.Ultraviolet(UV) emission with a high intensity at 375 nm was attributed to the excitation emission from photoluminescence (PL) spectrum.In PLspectrum, we also found green emission with a low intensity and wide FWHM.This green emission came from deep level transition due to defect levels in ZnO film.The ratio of the intensity of UVemission to that of green emission was as high as 193, indicating a high quality of the samples.This high quality was also confirmed by Atomic Force Microscope (AFM) analysis.Two methods were used in order to get ZnO film with a high resistivity.One was annealing ZnO film every ten minutes under relative high pressure of oxygen (O₂) at 700,the other was N-doping by N₂.ZnO film with a high resistivity was successfully prepared.The resistivity was 5×10⁴Ω·cm and 1100Ω·cm, respectively, while that of untreated sample was as low as 0.65Ω·cm.Furthermore, N-doped sample had a higher resistivity and better photoluminescence properties than that of the sample obtained by annealing under oxygen.

Key words: ZnO film, Photoluminescence, Atomic force microscope (AFM)

CLC Number:

TrendMD:

WANG Xin-Qiang, YANG Ru-Sen, YANG Shu-Ren, WANG Jin-Zhong, LI Xian-Jie, YIN Jing-Zhi, Ong H. C., JIANG Xiu-Ying, GAO Chun-Xiao, DU Guo-Tong. Growth of ZnO Film by Plasma-assisted MOCVD[J]. Chem. J. Chinese Universities, 2002, 23(5): 927.

[1]	ZHOU Yonghui, LI Yao, WU Yuxuan, TIAN Jing, XU Longquan, FEI Xu. Synthesis of A Novel Photoluminescence Self-healing Hydrogel [J]. Chem. J. Chinese Universities, 2022, 43(2): 20210606.
[2]	YIN Shaoyun, ZHANG Luyin, WANG Zheng, PAN Mei. Glass-like Cuprous Iodide Complexes with Photoluminescence Tuning and Two-photon Emission Properties ^† [J]. Chem. J. Chinese Universities, 2020, 41(4): 646.
[3]	LIANG Longqi, CHEN Cailing, YU Ying, LI Yuxin, LI Chunguang, SHI Zhan. Synthesis, Luminescence and Cell Imaging Properties of Amino Acid Capped YVO₄∶Eu Nanoparticles ^† [J]. Chem. J. Chinese Universities, 2020, 41(3): 425.
[4]	JI Tianhao, TIAN Yanqing. Optical Properties and Applications of Halide-perovskite Nanocrystals^† [J]. Chem. J. Chinese Universities, 2018, 39(6): 1113.
[5]	SUN Riyong,CHEN Zeyu,YE Yanchun,CHEN Mingxian,TANG Huaijun,WANG Kaimin,WANG Zhengliang. Bis(2-phenylpyridine)(2,2'-bithiazole)iridium(Ⅲ) Hexafluorophosphate: Synthesis and Application in Neutral/Warm White Light-emitting Diodes^† [J]. Chem. J. Chinese Universities, 2018, 39(5): 869.
[6]	ZHANG Dan, YU Jinhai, LI Dongze, ZHOU Miao, ZHANG Ying. Preparation of High Quality Ag₂S Quantum Dots with Near-Infrared Emission and Their Applications in Bioimaging^† [J]. Chem. J. Chinese Universities, 2018, 39(4): 623.
[7]	LI Bing, YAO Mingguang, LI Chunjie, DU Mingrun, LIU Bingbing. Synthesis of Water-soluble C₆₀ Nanoparticles Under Ultrasonication and Investigation of Their Photoluminescence Property^† [J]. Chem. J. Chinese Universities, 2014, 35(5): 949.
[8]	ZHAO Shijia, ZHANG Weiwei, WANG Shuguang, XIAO Junping, GONG Chen, DU Mingrun, YAO Mingguang, LIU Bingbing. Synthesis of Hydrogenated Graphite Nanostructures and Their Size-dependent Photoluminescence^† [J]. Chem. J. Chinese Universities, 2014, 35(4): 711.
[9]	ZHANG Zhuolei, LI Dongze, LIU Zhihui, XIE Renguo. Synthesis and Photoelectric Properties of High Quality CuFeS₂ Nanocrystals with Tunable Sizes^† [J]. Chem. J. Chinese Universities, 2014, 35(12): 2505.
[10]	LI Bing, GAO Feng, YANG Guangmin, TIAN Miaomiao, QU Xuesong, ZHANG Xintong. Synthesis and Characterization of Graphene Film via Photo-chemical Reduction of Graphene Oxide^† [J]. Chem. J. Chinese Universities, 2014, 35(12): 2612.
[11]	XU Yu-Dong, ZHANG Zheng-Yong, KONG Ji-Lie, LI Guo-Dong, XIONG Huan-Ming. Photoluminescent ZnO Quantum Dots Coated by Polymethacrylamide and Their Application in Cell Imaging [J]. Chem. J. Chinese Universities, 2013, 34(7): 1565.
[12]	DU Yan-Yan, HUANG Ke-Ke, ZHANG Jia-Qi, WANG Chu-Chu, CHU Xue-Feng, HOU Chang-Min, FENG Shou-Hua. Photoluminescence Properties of La_1/3NbO₃：Sm³⁺ Codoped with Sr²⁺, Ba²⁺ and Bi³⁺ Under Near-UV Excitation [J]. Chem. J. Chinese Universities, 2013, 34(3): 509.
[13]	HU Ya-Wei, HE Hui-Rong, MA Yang-Min, YANG Xiu-Fang. Fabrication and Wettability Conversion of ZnO/Ag Composite Films [J]. Chem. J. Chinese Universities, 2013, 34(2): 295.
[14]	GUAN Qiu-Mei, ZHANG Hui-Chao, YE Yong-Hong, CUI Yi-Ping, ZHANG Jia-Yu. Porous ZnO Thin Films by Gas Evaporation Method and Their Photovoltaic Properties [J]. Chem. J. Chinese Universities, 2012, 33(10): 2315.
[15]	WANG Shan-Shan, WANG Xue-Ting, GUO Ming-Ming, YU Jun-Sheng. Ligand Effects on Selective Interaction of CdTe Quantum Dots with BSA [J]. Chem. J. Chinese Universities, 2012, 33(06): 1195.

Growth of ZnO Film by Plasma-assisted MOCVD

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments