Influence Factors on Induced Potential of Reduced Graphene Oxide-based Microfluidic Voltage Generations

doi:10.7503/cjcu20230033

Abstract

Abstract:

In this paper， reduced graphene oxide（rGO）-based microfluidic voltage generations were fabricated with the suspensions at different rGO concentration. Different values of the induced potential of these rGO-based micro- fluidic voltage generations were generated at various volume flow rate of NaCl solution. Based on Nernst-Planck equation the quantitative relationship between the Na⁺ ion concentration in the diffusion layer upon the surface of the working electrode and induced potential of the microfluidic voltage generation was established. With the values of induced potential corresponding to different volume flow rates of the NaCl solution， the effect of the volume flow rate on both mass transporting of Na⁺ ions from the solution upon the rGO membranes and the concentration of the Na⁺ ion adsorbed on the surface of working electrode， and further the induced potential of the rGO-based microfluidic voltage generation had been researched. Besides， by quantitatively characterizing the surface morphology of the rGO membrane with the surface texture aspect ratio（Str） and maxium height（Sz）， the relationship among the rGO concentration of the suspension， the surface morphology of the rGO membrane， the concentration of the Na⁺ ion adsorbed on the surface of the working electrode and the induced potential of the microfluidic voltage generation had been established. At volume flow rate 50 μL/min of the NaCl solution and rGO concentration 1.0 mg/mL of the suspension the rGO-based microfluidic voltage generation can generate an optimal induced potential -343 mV. These results benefit not only the fabrication and performance optimizations of other carbon-based microfluidic voltage generations， but also the behavior improvements of the microfluidic channel based photo-degradation reactors， ion sensing devices and electrochemical glucose sensors.

Key words: Microfluidic voltage generator, Volume flow rate, Surface morphology, Ion concentration, Induced potential

CLC Number:

O646.2

TrendMD:

GAO Weizhuo, JING Weixuan, DU Yanrui, LI Zehao, HAN Feng, ZHAO Libo, YANG Zhaochu, JIANG Zhuangde. Influence Factors on Induced Potential of Reduced Graphene Oxide-based Microfluidic Voltage Generations[J]. Chem. J. Chinese Universities, 2023, 44(8): 20230033.

Figures/Tables 11

References 11

11	闵伶俐，陈松月，盛智芝，王宏龙，吴锋，王苗，侯旭. 物理学报， 2016， 65， 178301
12	Lv Y.， Gong F.， Li H.， Zhou Q.， Wu X.， Wang W.， Xiao R.， Appl. Energy， 2020， 279， 115764
13	Wang T.， Wang H.， Sci. Sin. Chim.， 2019， 49， 729—740
14	Zhao Y.， Song L.， Deng K.， Liu Z.， Zhang Z.， Yang Y.， Wang C.， Yang H.， Jin A.， Luo Q.， Gu C.， Xie S.， Sun L.， Adv. Mater.， 2008， 20， 1772
15	Liu J.， Dai L.， Baur J. W.， J. Appl. Phys.， 2007， 101， 343
16	Yin J.， Li X.， Yu J.， Zhang Z.， Zhou J.， Guo W. L.， Nat. Nanotechnol.， 2014， 9， 378—383
17	Ishigami M.， Chen J. H.， Cullen W. G.， Fuhrer M. S.， Williams E. D.， Nano Lett.， 2007， 7（6）， 1643—1648
18	Bolotin K. I.， Sikes K. J.， Jiang Z.， Klima M.， Fudenberg G.， Hone J.， Kim P.， Stormer H. L.， Solid State Communications， 2008， 146（9/10）， 351—355
19	Wang Y. Q.， Li J. H.， Peng Y.， Zhao Y. H.， Bai L. C.， Acta Phys. Sin.， 2021， 70， 206802
	王延庆，李佳豪，彭勇，赵又红，白利春. 物理学报， 2021， 70， 206802
20	Jiao S. P.， Liu M.， Li Y.， Abrha H.， Wang J.， Dai Y. X.， Li J. Y.， Kang N.， Li Y. X.， Liu X. H.， Carbon， 2022， 193， 339—355
21	Han Y. Y.， Zhang Z. P.， Qu L. T.， FlatChem， 2019， 14， 100090
22	Yin J.， Zhang Z. H.， Li X. M.， Yu J.， Zhou J. X.， Chen Y. Q.， Guo W. L.， Nat. Commun.， 2014， 5， 3582
23	Xue G.， Xu Y.， Ding T.， Li J.， Yin J.， Fei W.， Cao Y.， Yu J.， Yuan L.， Gong L.， Nat. Nanotechnol.， 2017， 12， 317
24	Alessandro S.， Philippe P.， Anne⁃Laure B.， Rémy F.， Xavier B.， Purcell S. T.， Lydéric B.， Nature， 2013， 494， 455—458
25	Lao J.， He Y.， Li X.， Yang T.， Zhu M.， Zhang Y.， Sun P.， Zhen Z.， Cheng B. F.， Nano Research， 2015， 8， 2467—2473
26	Arun R. K.， Singh P.， Biswas G.， Chanda N.， Chakraborty S.， Lab Chip， 2016， 16， 3589—3596
27	Guo W.， Cheng C.， Wu Y.， Jiang Y.， Gao J.， Li D.， Jiang L.， Adv. Mater.， 2013， 25， 6064—6068
28	Wang J.， Translated by Zhu Y. C.， Zhang L.， Analytical Electrochemistry，Chemical Industry Press， Beijing， 2008， 1—20
	约瑟夫王著，朱永春，张玲译，分析电化学，北京：化学工业出版社， 2008， 1—20
29	Zha Q. X.， Introduction to the Kinetics of Electrode Process， Science Press， Beijing， 2002， 74—127
	查全性. 电极过程动力学导论，北京：化学工业出版社， 2002， 74—127
30	Zhao P.， Qin N.， Wen J. Z.， Ren C. L.， Appl. Catal. B： Environ.， 2017， 209， 468—475
31	Jayamohana H.， Smith Y. R.， Hansen L. C.， Mohanty S. K.， Gale B. K.， Misra M.， Appl. Catal. B： Environ.， 2015， 174/175， 167—175
32	Jing W. X.， Gao W. Z.， Li Z. H.， Peng M. L.， Han F.， Wei Z. Y.， Yang Z. C.， Jiang Z. D.， Langmuir， 2021， 26， 37
33	Gao W. Z.， Jing W. X.， Li Z. H.， Wu Q.， Han F.， Zhao L. B.， Yang Z. C.， Jiang Z. D.， Microelectr. Engin.， 2022， 263， 111843
1	Ma X. Q.， Zhou S. X.， Energ. Convers. Manage.， 2022， 254， 115223
2	Singh P.， Sharma K.， Puchades I.， Agarwal P. B.， Sensor. Actuat. A： Phys.， 2022， 338， 113456
3	Kumar A.， Varghese A.， Sharma A.， Prasad M.， Janyani V.， Yadav R. P.， Elgaid K.， Sensor. Actuat. A： Phys.， 2022， 347， 113887
4	Xie T.， Wang C. L.， Yu C. F.， Micromotors， 2019， 52， 72
	解甜，王传礼，喻曹丰. 微电机， 2019， 52， 72
5	Sood A. K.， Ghosh S.， Phys. Rev. Lett.， 2004， 93， 099901
6	Dhiman P.， Yavari F.， Mi X.， Gullapalli H.， Shi Y.， Ajayan P. M.， Koratkar N.， Nano Lett.， 2011， 11， 3123—3127
7	Li X.， Sun P.， Fan L.， Zhu M.， Wang K.， Zhong M.， Wei J.， Wu D.， Cheng Y.， Zhu H.， Sci. Rep.， 2012， 2， 395
8	Ghosh S.， Sood A. K.， Kumar N.， Science， 2003， 299， 1042—1044
9	Elvira K. S.， Solvas X. C.， Wootton R. C. R.， deMello A. J.， Nat. Chem.， 2013， 5（11）， 905—915
10	Whitesides G. M.， Nature， 2006， 442， 368—373
11	Min L. L.， Chen S. Y.， Sheng Z. Z.， Wang H. L.， Wu F.， Wang M.， Hou X.， Acta Phys. Sin.， 2016， 65， 178301

[1]	XU Lin, ZHANG Huanhuan, SHI Tongfei. Morphology Evolution of Thin Polystyrene Film During the Non-solvent Driven Dewetting Process^† [J]. Chem. J. Chinese Universities, 2016, 37(1): 174.
[2]	YUAN Zhenshan, XU Qiang, SANG Lin, DING Fei. Application of Dimethyl Sulfoxide as Solvent of Electrolyte Solution in Rechargeable Lithium Metal Batteries^† [J]. Chem. J. Chinese Universities, 2014, 35(9): 1994.
[3]	JING Wei-Xuan, NIU Ling-Ling, WANG Bing, CHEN Lu-Jia, QI Han, ZHOU Fan, JIANG Zhuang-De. Preparation and Characterization of a ZnO Nanowires-based Cylindrical Hierarchical Structure [J]. Chem. J. Chinese Universities, 2013, 34(7): 1585.
[4]	LIU Li-Fen, XU De-Zhi, MAO Pei-Qing, ZHANG Lin, GAO Cong-Jie. Preparation and Characterization of a Novel Polyimide-urethane Reverse Osmosis Composite Membrane Material [J]. Chem. J. Chinese Universities, 2012, 33(07): 1605.
[5]	WANG Zheng*, TU Chun-Ling. Synthesis of Amphiphilic Chitosan Derivatives and Their Self-aggregation Phenomenon [J]. Chem. J. Chinese Universities, 2008, 29(2): 419.
[6]	CHEN Shun-Guo, SUN Jing-Zhi, HUANG Ji, WANG Mang . Effect of Substrate Temperature on Micro-structural Features of Zinc Perfluorophthalocyanine Thin Films [J]. Chem. J. Chinese Universities, 2005, 26(3): 511.
[7]	CAO Li-Zhi, LIANG Xiao-Cong, JIAO Jia-Jun, ZHUANG Si-Yong . Morphology of the Silver Iodobromide T-grain Crystal Surface [J]. Chem. J. Chinese Universities, 2005, 26(1): 142.